B_4C ceramics were fabricated by spark plasma sintering technique at 1700°C-1800C for 5 min under applied pressure of 50 MPa under vacuum atmosphere. Two different grades of B_4C powder from H.C. Starck Company namely HP grade and HS grade were used in all related experiments. Effect of sample geometry and dimensions as well as sample thickness on sintering parameters were analyzed. Samples having 5 mm thickness and 50 mm diameter, 8 mm thickness in circular geometries and 50 × 50 square cross-section, 8 mm thickness were fabricated. Using the powder, which provided the densest sample, yttrium oxide (Y_2O_3) was added, mixed and sintered. Optimization of SPS method production parameters for pure B_4C samples and B_4C samples with 5 wt% yttrium oxide additive were accomplished. The effect of geometry on density, Vickers hardness, fracture toughness, and microstructure were examined. The hardness and fracture toughness values of the samples were evaluated by the Vickers indentation technique.
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.