2014 | 125 | 2 | 362-364
Article title

Wear Behavior of TiAlN and CrAlN Coatings Deposited by TRD Process on AISI D2 Steel

Content
Title variants
Languages of publication
EN
Abstracts
EN
The wear properties of uncoated, chromium aluminum nitride (CrAlN) and titanium aluminum nitride (TiAlN) coated AISI D2 steel were investigated and compared using ball-on-disc method at 0.3 m/s sliding speed and under the loads of 2.5 N, 5 N, and 10 N against Si_3N_4 ball as a counter material. Steel samples were nitrided at 575C for 8 h in the first step of the coating process, and then titanium aluminum nitride coating and chromium aluminum nitride were performed by thermoreactive deposition (TRD) process at 1000C for 2 h. Coated samples were characterized by X-ray diffraction analysis, scanning electron microscopy, microhardness, and ball on disk wear tests. The results of friction coefficient and wear rate of the tested materials showed that the TiAlN coating presents the lowest results.
Keywords
EN
Contributors
author
  • Department of Metallurgical and Materials Engineering, Institute of Arts and Sciences, Sakarya University Esentepe Campus, 54187 Sakarya, Turkey
author
  • Korfez Technical and Industrial Vocational High School, Department of Metal Technology 41780, Korfez/Kocaeli, Turkey
author
  • Department of Metallurgical and Materials Engineering, Engineering Faculty, Sakarya University Esentepe Campus, 54187 Sakarya, Turkey
author
  • Department of Metallurgical and Materials Engineering, Engineering Faculty, Sakarya University Esentepe Campus, 54187 Sakarya, Turkey
References
  • 1. X.Z. Ding, C.T. Bui, X.T. Zeng, doi: 10.1016/j.surfcoat.2008.08.019, Surf. Coat. Technol. 203, 680 (2008)
  • 2. H. Unal, U. Sen, A. Mimaroglu, doi: 10.1016/j.matdes.2004.09.004, Mater. Des. 26, 705 (2005)
  • 3. K. Bobzin, E. Lugscheider, R. Nickel, N. Bagcivan, A. Kramer, doi: 10.1016/j.wear.2007.01.118, Wear 263, 1274 (2007)
  • 4. A. Liu, J. Deng, H. Cui, Y. Chen, J. Zhao, doi: 10.1016/j.ijrmhm.2011.09.010, Int. J. Refract. Met. Hard Mater. 31, 82 (2012)
  • 5. B. Gakovi, M. Trtica, B. Radak, S. Petrovi, P. Panjan, M. Cekada, T. Desai, D. Batani, doi: 10.1088/1464-4258/11/1/015601, J. Opt. A 11, 1 (2009)
  • 6. H. Scheerer, H. Hoche, E. Broszeit, B. Schramm, E. Abele, C. Berger, doi: 10.1016/j.surfcoat.2005.02.112, Surf. Coat. Technol. 200, 203 (2005)
  • 7. M. Uchida, N. Nihira, A. Mitsuo, K. Toyoda, K. Kubota, T. Aizawa, doi: 10.1016/S0257-8972Ž03.00937-X, Surf. Coat. Technol. 177-178, 627 (2004)
  • 8. X.Z. Ding, X.T. Zeng, SIMTech Tech. Rep. 6, 1 (2005)
  • 9. U. Sen, doi: 10.1016/j.matdes.2004.05.010, Mater. Des. 26, 167 (2005)
  • 10. O. Cegil, B. Kılınc, U. Sen, S. Sen, in: IMMC'16 Metallurgy & Materials Congress, Istanbul (Turkey), Eds.: A.F. Dericioglu, K. Kazmanli, S. Timur, C. Durucan, H. Savaş, UCTEA Chamber Of Metallurgical Engineers, Istanbul 2012, p. 453
  • 11. B. Kilinc, S. Sen, S. Demirkiran, U. Şen, doi: 10.12693/APhysPolA.123.268, Acta Phys. Pol. A 123, 268 (2013)
  • 12. B. Kilinc, S. Sen, U. Sen, doi: 10.12693/APhysPolA.123.271, Acta Phys. Pol. A 123, 271 (2013)
  • 13. C. Martini, G. Palombarini, G. Poli, D. Prandstraller, doi: 10.1016/j.wear.2003.10.003, Wear 256, 608 (2004)
  • 14. H.S. Benabdallah, R.J. Boness, doi: 10.1023/A:1004719910464, J. Mater. Sci. 34, 4995 (1999)
  • 15. V. Chawla, J. Mater. Sci. Eng. A 3, 22 (2013)
  • 16. V.H. Derflinger, A. Schutze, M. Ante, doi: 10.1016/j.surfcoat.2005.02.065, Surf. Coat. Technol. 200, 4693 (2006)
  • 17. H. Kim, C.Y. Kim, D.W. Kim, I.S. Lee, G.H. Lee, J.C. Park, S.J. Lee, K.Y. Lee, doi: 10.1088/1748-6041/5/4/044108, Biomed. Mater. 044108, 5 (2010)
  • 18. K.N. Andersen, E.J. Bienk, K.O. Schweitz, H. Reitz, J. Chevallier, P. Kringhøj, J. Bøttiger, doi: 10.1016/S0257-8972(99)00473-9, Surf. Coat. Technol. 123, 219 (2000)
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv125n2063kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.