Changes in Microstructure of Air Plasma Sprayed M-CrAlY Coatings After Short Thermal Exposure in Argon Atmosphere

• Authors: L. Čelko , V. Řičánková , L. Klakurková , T. Podrábský , E. Dvořáček , J. Švejcar
• Languages of publication: EN

Abstracts

EN

Conventional air plasma spray technique and two powders, NiCrAlY and CoNiCrAlY, were used to produce the M-CrAlY type of coating on the Inconel 713LC substrate. Two phase coatings, consisting of Ni and/or Co solid solution and NiAl intermetallic phase, were produced. A certain amount of imperfectly melted powder particles, voids and aluminium oxide was also present. After air plasma spraying the coatings were annealed at widely ranging temperatures (650, 800, 1000 and 1150°C) for two hours in argon-flow atmosphere. It was found that the temperature significantly affects the microstructure of resulting coatings. The oxide scale was formed by internal oxidation in a coating region primarily at higher temperatures. In this case, aluminium was depleted from the NiAl phase within the coating region and the Ni, Co, Cr solid solutions and the aluminium oxide started to form rapidly. No interaction was observed after the short thermal exposure below the substrate surface. The microstructure of coatings was recorded by scanning electron microscope. Coating thickness, amount of voids and oxide scale were measured by means of image analysis. The concentration of phases was estimated by energy dispersive microanalysis.

Keywords

EN

81.15.Rs

Discipline

• 81.15.Rs: Spray coating techniques

• Publisher: Institute of Physics, Polish Academy of Sciences
• Journal: Acta Physica Polonica A
• Year: 2011
• Volume: 120
• Issue: 2
• Pages: 336-339

Dates

published

2011-08

Contributors

author

L. Čelko

• Institute of Materials Science and Engineering, Faculty of Mechanical Engineering, Brno University of Technology, Technická 2, Brno 616 69, Czech Republic

author

V. Řičánková

• Institute of Materials Science and Engineering, Faculty of Mechanical Engineering, Brno University of Technology, Technická 2, Brno 616 69, Czech Republic

author

L. Klakurková

• Institute of Materials Science and Engineering, Faculty of Mechanical Engineering, Brno University of Technology, Technická 2, Brno 616 69, Czech Republic

author

T. Podrábský

• Institute of Materials Science and Engineering, Faculty of Mechanical Engineering, Brno University of Technology, Technická 2, Brno 616 69, Czech Republic

author

E. Dvořáček

• S.A.M. - Metallizing Company, Ltd., Hájecká 12, Brno, 618 00, Czech Republic

author

J. Švejcar

• Institute of Materials Science and Engineering, Faculty of Mechanical Engineering, Brno University of Technology, Technická 2, Brno 616 69, Czech Republic

References

• 1. M.J. Donachie, S.J. Donachie, Superalloys - A Technical Guide, ASM International, Ohio 2002)
• 2. M. Petrenec, K. Obrtlik, J. Polak, Key Eng. Mater. 348-349, 101 (2007)
• 3. M. Juliš, K. Obrtlík, S. Pospíšilová, T. Podrábský, J. Polák, Procedia Engineering 2, 1983 (2010)
• 4. Y. Tamarin, Protective Coatings for Turbine Blades , ASM International, Ohio 2002
• 5. T. Bose, High Temperature Coatings, Elsevier, Oxford 2007
• 6. L. Čelko, L. Klakurková, O. Man, J. Švejcar, Mater. Manufact. Process. 24, 1155 (2009)
• 7. T. Patterson, A. Leon, B. Jayaraj, J. Liu, Y.H. Sohn, Surf. Coat. Technol. 203, 437 (2008)
• 8. L. Huang, X.F. Sun, H.R. Guan, Z.Q. Hu, Surf. Coat. Technol. 201, 1421 (2006)
• 9. R.A. Mahesh, R. Jayaganthan, S. Prakash, Mater. Chem. Phys. 119, 449 (2010)
• 10. U. Dragos, M. Gabriela, B. Waltraut, C. Ioan, Solid State Sci. 7, 459 (2005)
• 11. D. Seo, K. Ogawa, M. Tanno, T. Shoji, S. Murata, Surf. Coat. Technol. 201, 7952 (2007)
• 12. D. Oquab, C. Estournes, D. Monceau, Adv. Eng. Mater. 9, 413 (2007)
• 13. M.C. Mayoral, J.M. Andrés, M.T. Bona, V. Higuera, F.J. Belzunce, Surf. Coat. Technol. 202, 1816 (2008)
• 14. Weizhou Li, Yueqiao Li, Chao Sun, Zhiliu Hu, Tianquan Liang, Wuquan Lai, J. Alloys Compd. (2010), 506, 77 (2010)
• 15. F.H. Yuan, Z.X. Chen, Z.W. Huang, Z.G. Wang, S.J. Zhu, Corros. Sci. 50, 1608 (2008)
• 16. J. Toscano, A. Gil, T. Hüttel, E. Wessel, D. Naumenko, L. Singheiser, W.J. Quadakkers, Surf. Coat. Technol. 202, 603 (2007)

Identifiers

DOI

10.12693/APhysPolA.120.336