Fabrication, Structure and Consolidation of NiAl-Al_2O_3 Mechanically Alloyed Nanocomposite Powders

• Authors: D. Oleszak , A. Michalski , T. Majewski
• Languages of publication: EN

Abstracts

EN

Reactive milling of NiO + Al powder mixture resulted in the formation of NiAl-Al_2O_3 nanocomposite powders, with a crystallite size of about 20 nm. The Hall-Williamson analysis revealed that NiAl showed an orientation dependent crystallite size after short processing time and orientation dependent internal strain after long milling time. Both anisotropies were removed by heating the powders in the differential scanning calorimetry. Calorimetric studies showed one exothermic effect attributed to the reduction reaction of NiO and endothermic one associated with melting of Al. Two methods were applied for powders compaction: resistance sintering and pulse electric discharge. In both cases the densities of about 90% of the theoretical value were achieved. A significant increase in average NiAl crystallites size in compacted samples was observed, up to several hundreds of nanometers.

Keywords

EN

81.20.Ev

Discipline

• 81.20.Ev: Powder processing: powder metallurgy, compaction, sintering, mechanical alloying, and granulation

• Publisher: Institute of Physics, Polish Academy of Sciences
• Journal: Acta Physica Polonica A
• Year: 2002
• Volume: 102
• Issue: 2
• Pages: 187-192

Dates

published

2002-08

received

2001-09-23

Contributors

author

D. Oleszak

• Faculty of Materials Science and Engineering, Warsaw University of Technology, Wołoska 141, 02-507 Warszawa, Poland

author

A. Michalski

• Faculty of Materials Science and Engineering, Warsaw University of Technology, Wołoska 141, 02-507 Warszawa, Poland

author

T. Majewski

• Department of Armament and Aviation, Military University of Technology, Kaliskiego 2, 00-908 Warsaw, Poland

References

• 1. P.G. McCormick, Mater. Trans. Jpn. Inst. Metals, 36, 161, 1995
• 2. P. Matteazzi, G. Le Caer, Mater. Sci. Eng. A, 156, 229, 1992
• 3. L. Froyen, in: Proc. Int. Conf. Light Alloys and Composites, May 1999, Zakopane, Poland, Eds. J. Dutkiewicz, S. Pietrowski, Lodart, Łódź 1999, p. 15
• 4. G.K. Williamson, W.H. Hall, Acta Met., 1, 22, 1953
• 5. D.G. Morris, A. Benghalem, Mater. Sci. Forum, 179-181, 11, 1995

Identifiers

DOI

10.12693/APhysPolA.102.187