2009 | 7 | 2 | 215-221

Article title

PbS nanostructures synthesized via surfactant assisted mechanochemical route

Content

Title variants

Languages of publication

EN

Abstracts

EN
PbS nanocrystals using surfactant assisted mechanochemical route has been successfully prepared. The methods of XRD, SEM, surface area and particle size measurements were used for nanocrystals characterization. The XRD patterns confirmed the presence of galena PbS (JCPDS 5–592) whatever treatment conditions were applied. The strong observable peaks indicate the highly crystalline nature in formation of PbS nanostructures where preferential crystal growth in the (200) direction after chelating agent (EDTANa2•2H2O) addition has been observed. The mean volume weighted crystallite size 4.9 nm and 35 nm has been calculated from XRD data using Williamson-Hall method for PbS synthesized without and/or with chelating agent, respectively corresponding with surface weighted crystallites sizes of 2.9 and 18.8 nm. The sample prepared without surfactant yields the smaller crystallites and the higher microstrain compared with surfactant assisted synthesis. The obtained results illustrate a possibility to manipulate crystal morphology by combining effect of milling and surfactant application. [...]

Publisher

Journal

Year

Volume

7

Issue

2

Pages

215-221

Physical description

Dates

published
1 - 6 - 2009
online
9 - 4 - 2009

Contributors

author
  • Institute of Geotechnics, Slovak Academy of Sciences, 043 53, Kosice, Slovakia
  • Mining Engineering Department, Sahand University of Technology, P.O.Box 51, 335/1996, Tabriz, Iran
  • Institute of Geotechnics, Slovak Academy of Sciences, 043 53, Kosice, Slovakia
  • Institute of Geotechnics, Slovak Academy of Sciences, 043 53, Kosice, Slovakia
  • Department of Microelectronics, Slovak University of Technology and International Laser Centre, 812 19, Bratislava, Slovakia
  • Department of Microelectronics, Slovak University of Technology and International Laser Centre, 812 19, Bratislava, Slovakia

References

  • [1] P.D. Yang, C.M. Lieber, Science 273, 1836 (1996) http://dx.doi.org/10.1126/science.273.5283.1836[Crossref]
  • [2] Y. Ni, H. Liu, F. Wang, Y. Liang, J. Hong, X. Ma, Z. Xu, Cryst. Res. Technol. 39, 200 (2004) http://dx.doi.org/10.1002/crat.200310171[Crossref]
  • [3] R. Houbertz, W. Krauss, R. Birringer, U. Hartmann, Nanostruct. Mater. 9, 339 (1997) http://dx.doi.org/10.1016/S0965-9773(97)00078-0[Crossref]
  • [4] D. Chen, K. Tang, G. Shen, J. Sheng, Z. Fang, X. Liu, H. Zheng, Y. Qian, Mater. Chem. Phys. 82, 206 (2003) http://dx.doi.org/10.1016/S0254-0584(03)00206-2[Crossref]
  • [5] J. Wang, X. Chen, Z. Wang, W. Yu, Y. Qian, Mater. Chem. Phys. 88, 217 (2004) http://dx.doi.org/10.1016/j.matchemphys.2004.07.013[Crossref]
  • [6] U.K. Gantam, R. Seshadri, Mater. Res. Bull. 39, 669 (2004) http://dx.doi.org/10.1016/j.materresbull.2003.12.003[Crossref]
  • [7] Q. Liu, Y. Ni, G. Yin, J. Hong, Z. Xu, Mater. Chem. Phys. 89, 379 (2005) http://dx.doi.org/10.1016/j.matchemphys.2004.09.017[Crossref]
  • [8] R.R. Hawalder, K.G. Kanade, K.R. Patil, S.D. Sathaye, U.P. Mulik, D.P. Amalnerkar, Mater. Chem. Phys. 91, 447 (2005) http://dx.doi.org/10.1016/j.matchemphys.2004.12.007[Crossref]
  • [9] S.F. Wang, F. Gu, M.K. Lü, G.J. Zhou, A.Y. Zhang, J. Cryst. Growth 289, 621 (2006) http://dx.doi.org/10.1016/j.jcrysgro.2005.11.100[Crossref]
  • [10] C. Li, G. Shi, H. Xu, S. Guang, R. Yin, Y. Song, Mater. Lett. 61, 1809 (2007) http://dx.doi.org/10.1016/j.matlet.2006.07.137[Crossref]
  • [11] Z. Xiu, S. Liu, J. Yu, F. Xu, W. Yu, G. Feng, J. Alloy. Compd. 457, L9 (2008) http://dx.doi.org/10.1016/j.jallcom.2007.03.060[Crossref]
  • [12] P. Baláz, E. Boldizárová, E. Godocíková, J. Briancin, Mater. Lett. 57, 1585 (2003) http://dx.doi.org/10.1016/S0167-577X(02)01037-6[Crossref]
  • [13] E. Dutková, P. Baláz, P. Pourghahramani, A.V. Nguyen, V. Sepelák, A. Feldhoff, J. Kovác, A. Satka, Solid State Ionics 179, 1242 (2008) http://dx.doi.org/10.1016/j.ssi.2008.03.020[Crossref]
  • [14] P. Baláz, Mechanochemistry in Nanoscience and Minerals Engineering (Springer Berlin, Heidelberg, 2008)
  • [15] P. Pourghahramani, E. Forssberg, Int. J. Miner. Process. 79, 120 (2006) http://dx.doi.org/10.1016/j.minpro.2006.01.010[Crossref]
  • [16] G.K. Williamson, W.H. Hall, Acta Metall. Mater. 1, 22 (1953) http://dx.doi.org/10.1016/0001-6160(53)90006-6[Crossref]
  • [17] Y. Wang, B. Zhao, F. Zhang, W. Mao, G. Qian, X. Fan, Mater. Lett. 61, 3733 (2007) http://dx.doi.org/10.1016/j.matlet.2006.12.085[Crossref]
  • [18] P. Pourghahramani, E. Forssberg, Int. J. Miner. Process. 79, 106 (2006) http://dx.doi.org/10.1016/j.minpro.2006.02.001[Crossref]
  • [19] X.R. Ye, D.Z. Jia, J.Q. Yu, X.Q. Xin, Z.L. Xue, Adv. Mater. 11, 941 (1999) http://dx.doi.org/10.1002/(SICI)1521-4095(199908)11:11<941::AID-ADMA941>3.0.CO;2-T[Crossref]
  • [20] X. Wang, Ch. Xu, Z. Zhang, Mater. Lett. 60, 345 (2006) http://dx.doi.org/10.1016/j.matlet.2005.08.048[Crossref]
  • [21] D. Liang, S. Tang, J. Liu, J. Liu, X. Lu, L. Kang, Mater. Lett. 62, 2426 (2008) http://dx.doi.org/10.1016/j.matlet.2007.12.012[Crossref]
  • [22] S.M. Zhou, X.H. Zhang, X.M. Meng, X. Fan, S.T. Lee, S.K. Wu, J. Solid State Chem. 178, 399 (2005) http://dx.doi.org/10.1016/j.jssc.2004.06.034[Crossref]

Document Type

Publication order reference

Identifiers

YADDA identifier

bwmeta1.element.-psjd-doi-10_2478_s11532-009-0005-3
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.