In this work photocatalytic properties of TiO2 thin films doped with different amount of Tb have been described. Thin films were prepared by high energy reactive magnetron sputtering process. Comparable photocatalytic activity has been found for all doped TiO2 thin films, while different amounts of Tb dopant (0.4 and 2.6 at. %) results in either an anatase or rutile structure. It was found that the terbium dopant incorporated into TiO2 was also responsible for the amount of hydroxyl groups and water particles adsorbed on the thin film surfaces and thus photocatalytic activity was few times higher in comparison with results collected for undoped TiO2 thin films.
In this work, the influence of Tb-doping on structure, and especially hardness of nanocrystalline TiO2 thin films, has been described. Thin films were formed by a high-energy reactive magnetron sputtering process in a pure oxygen atmosphere. Undoped TiO2-matrix and TiO2:Tb (2 at. % and 2.6 at. %) thin films, had rutile structure with crystallite sizes below 10 nm. The high-energy process produces nanocrystalline, homogenous films with a dense and close packed structure, that were confirmed by X-ray diffraction patterns and micrographs from a scanning electron microscope. Investigation of thin film hardness was performed with the aid of a nanoindentation technique. Results of measurements have shown that the hardness of all manufactured nanocrystalline films is above 10 GPa. In the case of undoped TiO2 matrix, the highest hardness value was obtained (14.3 GPa), while doping with terbium results in hardness decreasing down to 12.7 GPa and 10.8 GPa for TiO2:(2 at. % Tb) and TiO2:(2.6 at. % Tb) thin films, respectively. Incorporation of terbium into TiO2-matrix also allows modification of the elastic properties of the films.
Transparent oxide semiconducting thin films based on mixed Ti-V oxides were prepared using a modified reactive magnetron sputtering method. Based on structural investigations performed with the help of x-ray diffraction and transmission electron microscopy analysis, two distinct regions in the prepared thin film have been observed: a nanocrystalline TiO2-V2O3-V2O5 mixed composition, and a thin layer consisting of amorphous phase and nanocystalline TiO2 phase deposited directly at the substrate. Optical measurements show excellent transmission in the visible spectral range of 73%, on average. Resistivity of the thin film was found at the order of 105 Ω cm at room temperature. The preparation of mixed Ti-V oxides provides a combination of high transparency and semiconducting properties.
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.