As revealed by Mössbauer spectroscopy, replacement of 10 at.% of iron in the amorphous Fe70Mo5Cr4Nb6B15 alloy by cobalt or nickel has no effect on the magnetic structure in the vicinity of room temperature, although the Curie point moves from 190 K towards ambient one. In the early stages of crystallization, the paramagnetic crystalline Cr12Fe36Mo10 phase appears before α-Fe or α-FeCo are formed, as is confirmed by X-ray diffractometry and transmission electron microscopy. Creation of the crystalline Cr12Fe36Mo10 phase is accompanied by the amorphous ferromagnetic phase formation at the expense of amorphous paramagnetic one.
EN
Mössbauer spectra and thermomagnetic curves for the Fe86−xMxZr7Nb2Cu1B4 (M = Co, Ni, CoCr, and Cr, x = 0 or 6) alloys in the as-quenched state and after the accumulative annealing in the temperature range 600–800 K for 10 min are investigated. The parent Fe86Zr7Nb2Cu1B4 amorphous alloy is paramagnetic at room temperature, and substitution of 6 at.% of Fe by Co, Ni, and CoCr changes the magnetic structure – the alloys become ferromagnetic, whereas replacing 6 at.% of Fe with Cr preserves the paramagnetic state. After the heat treatment at 600 K, the decrease of the average hyperfine field induction, as compared to the as-quenched state, is observed due to the invar effect. After this annealing, the Curie temperature for all investigated alloys decreases. The accumulative annealing up to 800 K leads to the partial crystallization; α-Fe or α-FeCo grains with diameters in the range of 12–30 nm in the residual amorphous matrix appear.