The relaxation processes and the properties of polymer/ceramic nanocomposites have been studied by the 1H nuclear magnetic resonance methods. Nanocomposites of poly(ethylene terephthalate) PET and poly(phenylene sulfide) PPS with 0.25, 2.5 and 5% wt. barium titanate BT were prepared using a twin screw extruder and injection moulding machine. The spin-lattice relaxation time T1, second moment M2 and the motional parameters as e.g. the activation energies in the nanocomposites were investigated.
Nano- and microemulsions containing as the oil phase caprylic/capric propylene glycol diesters (Crodamol PC) were investigated as potential vehicle for controlled release of geranic acid. The influence of emulsifiers and co-surfactants on stability of the emulsions was investigated. Different kind of polysorbates (ethoxylated esters of sorbitan and fatty acids) were applied as the emulsifiers. The short-chain alcohols (ethanol, 1-propanol, 1-butanol) were used as co-surfactants. The emulsions were prepared at ambient temperature (25°C), by the phase inversion composition method (PIC). The stable O/W high dispersed emulsion systems based on Crodamol PC, of mean droplets size less than 200 nm, were prepared. Microemulsions stabilized by the mixture of Polisorbat 80 and 1-butanol were characterized by the largest degree of dispersion (137 nm) and the lowest PDI value (0.094), at surfactant/co-surfactant: oil weight ratio 90:10. The stable nano-emulsion (mean droplet size of 33 nm) was obtained for surfactant: oil (S:O) weight ratio 90:10, without co-surfactant addition. This nano-emulsion was chosen to release studies. The obtained results showed that the prepared stable nano-emulsion can be used as a carrier for controlled release of geranic acid. The active substance release from the nano-emulsion and the oil solution, after 24 hours was 22%.
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.