The effect of deformation route in equal channel angular pressing on mechanical properties of aluminum alloy 1050

Content
Title variants
Languages of publication
PL
Abstracts
PL
Annealed samples of commercial purity aluminium (1050) were processed by Equal Channel Angular Pressing (ECA P) at room temperature for up to eight passes. ECA P was conducted by using three processing routes (schemes). Tensile tests and micro hardness were conducted to evaluate variation of mechanical properties after each pass. Analysis of fractography was carried out due to investigate a fracture of the samples. The results showed that all the schemes had similar micro hardness values – around 50 HV. The tensile test results showed that the highest yield strength was achieved in the second scheme after eight passes – 186 MPa – while elongation maintained at the level of 17.4%. The value of yield strength achieved increased more than six times in proportion to annealed condition.
Publisher
Year
-
Physical description
Dates
online
2016-03-15
Contributors
References
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.ojs-nameId-6e3e8ea9-5a94-37a7-828b-e6cd5da23db6-year-2016-article-5933
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.