The MBE grown ZnYbTe layers were characterized by X-ray diffraction, photoluminescence and reflectivity measurements. The MBE growth conditions allowing to obtain monocrystalline ZnYbTe layers were found to be metal-rich (MBE growth with excess of Zn flux). In optical measurements (photoluminescence, reflectivity), both transitions connected with ternary ZnYbTe compound and with Yb^{3+} ions were detected. The quality of ZnYbTe layers with Yb content of 3% and 1% is inferior to the quality of pure ZnTe MBE layers, which is clearly seen in the results of photoluminescence and reflectivity measurements. In the ZnYbTe layers with 3% Yb, exhibiting monocrystalline character in reflection high-energy electron diffraction and X-ray diffraction measurements, optical transitions characteristic of pure YbTe were detected. In ZnYbTe layers with 1% Yb, no transitions connected with YbTe were observed.
Journal
Year
Volume
Issue
Pages
1060-1064
Physical description
Dates
published
1996-11
Contributors
author
- Institute of Physics, Polish Academy of Sciences, Al. Lotników 32/46, 02-668 Warszawa, Poland
author
- Institute of Physics, Polish Academy of Sciences, Al. Lotników 32/46, 02-668 Warszawa, Poland
author
- Institute of Physics, Polish Academy of Sciences, Al. Lotników 32/46, 02-668 Warszawa, Poland
author
- Institute of Physics, Polish Academy of Sciences, Al. Lotników 32/46, 02-668 Warszawa, Poland
author
- Universite Montpellier 2, Place E. Bataillon, Montpellier, France
author
- Universite Montpellier 2, Place E. Bataillon, Montpellier, France
References
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv90z547kz