Article title

Transport Properties in 2,6-Diamino Anthraquinone

Authors

Content

Title variants

Languages of publication

EN

Abstracts

EN
Current density-voltage characteristics were obtained from 2,6-diamino anthraquinone samples using ohmic aluminium electrodes. Results showed that at low voltage the conduction process was ohmic, while at high voltage space-charge-limited conduction controlled by a single dominant trap level was presented. Thickness dependence measurements proved that the trapping sites were located at a discrete energy level. The transition voltage, V, between ohmic and space-charge-limited conduction was approximately proportional to the square of the sample thickness and was found to be temperature independent. The temperature dependence of ohmic and space-charge-limited current densities have been investigated. The results were interpreted in terms of extrinsic nature of ohmic conduction. Traps with density ≈ 2 × 10^{24} m^{-3} located at 0.50 ± 0.03 eV below the conduction band edge have been observed.

Keywords

EN

Contributors

author
  • Physics Department, Alexandria University, Alexandria, Egypt
author
  • Physics Department, El-Minia University, El-Minia, Egypt

References

Document Type

Publication order reference

Identifiers

YADDA identifier

bwmeta1.element.bwnjournal-article-appv85z606kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.