2017 | 131 | 4 | 1105-1107
Article title

The Effect of Cryo-Rolling and Annealing on Magnetic Properties in Non-Oriented Electrical Steel

Title variants
Languages of publication
The goal of the present work is to compare progressive technology - rolling at cryogenic temperature and classical rolling at ambient temperature followed by an investigation of their impact on the final microstructure and the magnetic properties of non-oriented electrical steel. Non-oriented electrical steel is characterized by high magnetic induction, low magnetic losses, and low coercivity. The best magnetic properties are achieved using preferable texture and optimal grain size. In this paper there is analyzed the percentage of different textural components after cryo-rolling and after rolling at ambient temperature. To obtain maps of inverse pole figures, the electron backscatter diffraction method was used. The main contribution of this study was that the samples rolled at cryo conditions and after final annealing reached better magnetic properties than at ambient temperature, which was reflected by low magnetic losses and coercivity.
Physical description
  • [1] R. Bidulský, M.A. Grande, L. Ferraris, P. Ferraris, J. Bidulská, Acta Phys. Pol. A 118, 802 (2010), doi: 10.12693/APhysPolA.118.802
  • [2] R. Bidulský, J. Bidulská, M.A. Grande, L. Ferraris, Acta Metall. Slov. 20, 271 (2014), doi: 10.12776/ams.v20i3.351
  • [3] T. Kvačkaj, J. Bidulská, R. Biduslký, A. Kováčová, R. Kočiško, P. Bella, M. Lupták, J. Bacsó, Acta Phys. Pol. A 126, 184 (2014), doi: 10.12693/APhysPolA.126.184
  • [4] R.Z. Valiev, I.V. Alexandrov, Y.T. Zhu, T.C. Lowe, J. Mater. Res. 17, 5 (2002), doi: 10.1007/s10853-015-9354-9
  • [5] Y.M. Wang, M.W. Chen, F. Zhou, E. Ma, Nature 419, 912 (2002), doi: 10.1038/533284a
  • [6] J. Salinas-Beltrán, A. Salinas-Rodríguez, E. Gutiérrez-Castañeda, R. Deaquino Lara, J. Magn. Magn. Mater. 406, 159 (2016), doi: 10.1016/j.jmmm.2016.01.017
  • [7] K. Matsumura, B. Fukunda, IEEE Trans. Magn. 20, 1533 (1984), doi: 10.1109/TMAG.1984.1063223
  • [8] E.T. Stephenson, A.R. Marder, IEEE Trans. Magn. 22, 101 (1986), doi: 10.1109/TMAG.1986.1064281
  • [9] F. Kováč, M. Dzubinský, Y. Sidor, J. Magn. Magn. Mater. 269, 333 (2004), doi: 10.1016/S0304-8853(03)00628-0
  • [10] S.K. Chen, Q.Y. Li, Z. Miao, F. Xu, Rare Metal Mater. Eng. 35, 500 (2006)
  • [11] T. Kvačkaj, R. Kočiško, R. Bidulský, J. Bidulská, P. Bella, M. Lupták, A. Kováčová, J. Bacsó, Mater. Sci. Forum 782, 379 (2014), doi: 10.4028/
  • [12] T. Kvačkaj, J. Bidulská, Adv. Mater. Res. 842, 783 (2014), doi: 10.4028/
  • [13] T. Kvačkaj, J. Bacsó, J. Bidulská, M. Lupták, I. Pokorný, M. Kvačkaj, M. Vlado, Acta Metall. Slov. 16, 268 (2010), doi: 10.12776/ams.v20i3.351
  • [14] T. Kvačkaj, Metalurgija 39, 185 (2000)
Document Type
Publication order reference
YADDA identifier
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.