Development of Magnetic Properties during Annealing of Hf₂Co₁₁B Amorphous Alloy

• Authors: A. Musiał , Z. Śniadecki , B. Idzikowski
• Languages of publication: EN

Abstracts

EN

Influence of heat treatment on magnetic properties of amorphous Hf₂Co₁₁B alloy was investigated. Hard magnetic phase, characterized by high magnetic anisotropy, appears during crystallization. The highest coercive field equal to 1.86 kOe, was obtained for sample annealed in third crystallization stage. Longer heat treatment at T_{a} = 650°C leads to decrease in coercive field, which can be the result of excess of the HfCo₃B₂ phase volume fraction and additionally eutectoid transformation of hard magnetic phase into soft magnetic Co₂₃B₆ and fcc-Co. Decrease of volume fraction of hard phase is confirmed by the remanence ratio m_{r}. Value of m_{r}, for T_{a} = 650°C, is decreasing with annealing time from 0.4 to 0.27 for 30 min and 120 min, respectively. The magnetocrystalline anisotropy constant K₁ increases from 2.23 Merg/cm³ for the amorphous ribbon to 15.84 Merg/cm³ for the sample annealed at 650°C for 30 min.

Keywords

EN

75.50.Ww; 75.60.Nt; 75.50.Kj

Discipline

• 75.60.Nt: Magnetic annealing and temperature-hysteresis effects
• 75.50.Kj: Amorphous and quasicrystalline magnetic materials
• 75.50.Ww: Permanent magnets(for magnets, see 07.55.Db in instruments)

• Publisher: Institute of Physics, Polish Academy of Sciences
• Journal: Acta Physica Polonica A
• Year: 2017
• Volume: 131
• Issue: 4
• Pages: 786-788

Dates

published

2017-04

Contributors

author

A. Musiał

• Institute of Molecular Physics, Polish Academy of Sciences, M. Smoluchowskiego 17, 60-179 Poznań, Poland
• Nanobiomedical Centre, Adam Mickiewicz University in Poznań, Umultowska 85, 61-614 Poznań, Poland

author

Z. Śniadecki

• Institute of Molecular Physics, Polish Academy of Sciences, M. Smoluchowskiego 17, 60-179 Poznań, Poland

author

B. Idzikowski

• Institute of Molecular Physics, Polish Academy of Sciences, M. Smoluchowskiego 17, 60-179 Poznań, Poland

References

• [1] O. Gutfleisch, M.A. Willard, E. Brück, C.H. Chen, S.G. Sankar, J.P. Liu, Adv. Mater. 23, 821 (2011), doi: 10.1002/adma.201002180
• [2] B. Idzikowski, M. Wolf, A. Handstein, K. Nenkov, H.-J. Engelmann, F. Stobiecki, K.-H. Muller, IEEE Trans. Magn. 33, 3559 (1997), doi: 10.1109/20.619497
• [3] A. Pasko, F. Mazaleyrat, M. LoBue, E. Fazakas, L.K. Varga, EPJ Web Conf. 40, 6008 (2013), doi: 10.1051/epjconf/20134006008
• [4] A. Edström, M. Werwiński, D. Iuşan, J. Rusz, O. Eriksson, K.P. Skokov, I.A. Radulov, S. Ener, M.D. Kuz'min, J. Hong, M. Fries, D.Y. Karpenkov, O. Gutfleisch, P. Toson, J. Fidler, Phys. Rev. B. 92, 174413 (2015), doi: 10.1103/PhysRevB.91.024504
• [5] H.W. Chang, M.C. Liao, C.W. Shih, W.C. Chang, C.C. Yang, C.H. Hsiao, H. Ouyang, Appl. Phys. Lett. 105, 192404 (2014), doi: 10.1063/1.4901737
• [6] G.D. Yüzüak, E. Yüzüak, Y. Elerman, J. Alloys Comp. 681, 589 (2016), doi: 10.1016/j.jallcom.2016.04.149
• [7] A. Musiał, Z. Śniadecki, B. Idzikowski, Mater. Des. 114, 404 (2017), doi: 10.1016/j.matdes.2016.11.004
• [8] A. Musiał, Z. Śniadecki, J. Marcin, J. Kováč, I. Škorvánek, B. Idzikowski, J. Alloys Comp. 665, 93 (2016), doi: 10.1016/j.jallcom.2015.12.186
• [9] M.A. McGuire, O. Rios, N.J. Ghimire, M. Koehler, Appl. Phys. Lett. 101, 202401 (2012), doi: 10.1063/1.4766283
• [10] G. Hadjipanayis, D.J. Sellmyer, B. Brandt, Phys. Rev. B. 23, 3349 (1981), doi: 10.1103/PhysRevB.23.3349
• [11] B. Das, B. Balamurugan, P. Kumar, R. Skomski, V.R. Shah, J.E. Shield, A. Kashyap, D.J. Sellmyer, IEEE Trans. Magn. 49, 3330 (2013), doi: 10.1109/TMAG.2013.2242856
• [12] E.F. Kneller, R. Hawig, IEEE Trans. Magn. 27, 3588 (1991), doi: 10.1109/20.102931
• [13] W.S. Sun, H.F. Zhang, Z.Q. Hu, T. Kulik, J. Non. Cryst. Solids 351, 1696 (2005), doi: 10.1016/j.jnoncrysol.2005.04.064
• [14] X. Lu, K. Cheng, S. Liu, K. Li, F. Zheng, Y. Du, J. Alloys Comp. 627, 251 (2015), doi: 10.1016/j.jallcom.2014.03.167
• [15] H. Ido, M. Nanjo, M. Yamada, J. Appl. Phys. 75, 7140 (1994), doi: 10.1063/1.356704
• [16] W.Y. Zhang, X.Z. Li, S. Valloppilly, R. Skomski, J.E. Shield, D.J. Sellmyer, J. Phys. D Appl. Phys. 46, 135004 (2013), doi: 10.1088/0022-3727/46/13/135004

Identifiers

DOI

10.12693/APhysPolA.131.786