Mechanical Properties of Soda-Lime-Silica Glasses with Variable Peanut Shell Contents

Content
Title variants
Languages of publication
EN
Abstracts
EN
In this study, the mechanical properties of soda-lime-silica glasses were investigated by using micro-Vickers indentation tests, while varying the amount of peanut shell powder added to the glass. Peanut shell powder was obtained by grinding peanut shells. It was added as a dopant to glass at 0.5-5 wt.%, with the final glass samples being produced by melting. Peanut shell addition had led to a decreased density of the soda-lime-silica glasses, and X-ray diffraction data of the peanut shell-doped soda-lime-silica glasses indicated the presence of two crystalline phases, namely, anorthite (Na_{0.45}(Ca_{0.55}Al_{1.55}Si_{2.45}O₈) and magnesium aluminum silicate (MgAl₂Si₃O_{10})₆. The Young's modulus values of the soda-lime-silica glasses increased along with the amount of peanut shell powder added. Peanut shell addition to the soda-lime-silica glasses has also caused increased hardness. Fracture toughness values of these glass samples were in the range of 0.91-1.04 MPa m^{1/2}. Thus, the mechanical properties (e.g. E and K_{C}) of soda-lime-silica glasses could be enhanced through peanut shell addition.
Keywords
EN
Year
Volume
131
Issue
3
Pages
511-513
Physical description
Dates
published
2017-03
References
  • [1] G. Tammann, The States of Aggregation, D. Van Nostrand, New York 1925, p. 297
  • [2] W.H. Zachariasen, J. Am. Chem. Soc. 54, 3841 (1932), doi: 10.1021/ja01349a006
  • [3] W. Vogel, Chemistry of Glass, The American Ceramic Society, Columbus, OH 1985, p. 113
  • [4] J.E. Stanworth, Physical Properties of Glass, Oxford University Press, London 1950, p. 39
  • [5] T. Uchino, K. Nakaguchi, Y. Nagashima, T. Kondo, J. Non-Cryst. Solids 261, 72 (2000), doi: 10.1016/S0022-3093(99)00617-1
  • [6] L. Pilon, F. Janos, R. Kitamura, J. Am. Ceram. Soc. 97, 442 (2014), doi: 10.1111/jace.12768
  • [7] E. Kilinc, R.J. Hand, J. Non-Cryst. Solids 429, 190 (2015), doi: 10.1016/j.jnoncrysol.2015.08.013
  • [8] G.R. Anstis, P. Chantikul, B.R. Lawn, D.B. Marshall, J. Am. Ceram. Soc. 64, 533 (1981), doi: 10.1111/j.1151-2916.1981.tb10320.x
  • [9] S. Lopez-Esteban, J.F. Bartolome, L.A. Dıaz, L. Esteban-Tejeda, C. Prado, R. Lopez-Piriz, R. Torrecillas, J.S. Moya, J. Mech. Behav. Biomed. Mater. 34, 302 (2014), doi: 10.1016/j.jmbbm.2014.02.019
  • [10] M.M. Smedskjaer, M. Jensen, Y. Yue, J. Non-Cryst. Solids 356, 893 (2010), doi: 10.1016/j.jnoncrysol.2009.12.030
Document Type
Publication order reference
YADDA identifier
bwmeta1.element.bwnjournal-article-appv131n349kz
Identifiers
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.