Effect of Heat Treatment and Pulse Plasma Process on Surface Properties of Steels

• Authors: Y. Özbek
• Languages of publication: EN

Abstracts

EN

The aim of this study was to examine the effect of heat treatment and pulse plasma treatment on surface properties of AISI 1050 steel used in this work. Firstly, the heat treatment was applied to samples for 2 h at 860°C. The quenching media were selected as water and oil and air cooling was applied. The tempering process was applied at different temperatures like 600°C, 500°C, 400°C and 100°C. Having completed the heat treatment, the pulse plasma process was applied to all samples. The surfaces were investigated with optic microscope, scanning electron microscopy, and X-ray diffraction analyses. The hardness testing was done for all samples from surface to center. The mechanical properties were improved after pulse plasma treatment.

Keywords

EN

81.65.Lp

Discipline

• 81.65.Lp: Surface hardening: nitridation, carburization, carbonitridation

• Publisher: Institute of Physics, Polish Academy of Sciences
• Journal: Acta Physica Polonica A
• Year: 2017
• Volume: 131
• Issue: 1
• Pages: 182-185

Dates

published

2017-01

Contributors

author

Y. Özbek

• Sakarya University, Engineering Faculty, Department of Metallurgical and Materials Engineering, Esentepe Campus, 54187, Sakarya, Turkey

References

• [1] C.T. Kwok, F.T. Cheng, H.C. Man, Surf. Coat. Technol. 200, 3544 (2006), doi: 10.1016/j.surfcoat.2004.12.016
• [2] B.N. Mordyuk, G.I. Prokopenko, P.Yu. Volosevich, L.E. Matokhnyuk, A.V. Byalonovich, T.V. Popova, Mater. Sci. Eng. 659, 119 (2016), doi: 10.1016/j.msea.2016.02.036
• [3] N.N. Cherenda, V.V. Uglov, A.K. Kuleshov, V.M. Astashynski, A.M. Kuzmitski, Vacuum 129, 170 (2016), doi: 10.1016/j.vacuum.2016.03.019
• [4] Shengzhi Hao, Limin Zhao, Yanlong Zhang, Huihui Wang, Nucl. Instrum. Methods Phys. Res. B 356, 12 (2015), doi: 10.1016/j.nimb.2015.04.046
• [5] Alloy Information for AISI 1050 Carbon Steel, All Metals & Forge Group http://steelforge.com/aisi-1050
• [6] R. Prasad, S. Kumar, J. Mater. Process. Technol. 42, 51 (1994), doi: 10.1016/0924-0136(94)90074-4
• [7] Y.Y.Özbek, M. Durman, H. Akbulut, Tribol. Trans. 52, 213 (2009), doi: 10.1080/10402000802369721
• [8] Y.Y. Ozbek, C. Sarioglu, M. Durman, Vacuum 106, 11 (2014), doi: 10.1016/j.vacuum.2014.03.001
• [9] J.S. Chen, C. Yu, H. Lu, J. Alloys Comp. 625, 224 (2015), doi: 10.1016/j.jallcom.2014.11.130
• [10] C. Binder, T. Bendo, G. Hammes, A.N. Klei, J.D.B. de Mello, Wear 332-333, 995 (2015), doi: 10.1016/j.wear.2015.01.083
• [11] Y.Y.Özbek, M. Durman, Mater. Technol. 49, 441 (2015), doi: 10.17222/mit.2013.219

Identifiers

DOI

10.12693/APhysPolA.131.182