2017 | 131 | 1 | 153-155
Article title

Electrical Conductivity and Corrosion Performances of In Situ and Ex Situ AA7075 Aluminum Composites

Content
Title variants
Languages of publication
EN
Abstracts
EN
The present study investigates corrosion behaviors and electric conductivity of AA7075 in situ (TiAl₃) and ex situ (B₄C) composites produced by powder metallurgy method. In production of in situ composites, various amounts of Ti (2, 4 and 6%) are added to AA7075 and for production of ex situ composites, B₄C (3, 6, and 9%) are added. Prepared in situ and ex situ composite powders were pre-shaped at 600 MPa pressure with cold pressing. Pre-shaped samples were sintered in the atmosphere-controlled furnace at 580°C for 4 h. Corrosion test of produced composites was conducted in 0.1 M H₂SO₄ solution. As a result of these analyses, corrosion examinations on in situ manufactured composites revealed that anode and cathode currents are close to each other and those composites do not exhibit different corrosion behaviors. Corrosion rate of B₄C added ex situ composites increases by B₄C rate (due to increase of density of current).
Keywords
EN
Publisher

Year
Volume
131
Issue
1
Pages
153-155
Physical description
Dates
published
2017-01
Contributors
author
  • Karabuk University, Technology Faculty, Manufacturing Engineering, 78100 Karabuk, Turkey
author
  • Karabuk University, Technology Faculty, Manufacturing Engineering, 78100 Karabuk, Turkey
author
  • Hitit University, Faculty of Engineering, Chemical Eng., 19100 Corum, Turkey
References
  • [1] D. Özyürek, R. Yılmaz, E. Kibar, J. Fac. Eng. Archit. Gaz. 27, 193 (2012)
  • [2] R. Yılmaz, D. Özyürek, E. Kibar, J. Fac. Eng. Archit. Gaz. 27, 429 (2012)
  • [3] K.M. Il, K.S. Lee, J. Alloys Comp. 264, 258 (1998), doi: 10.1016/S0925-8388(97)00262-4
  • [4] H. Zhao, J. Wang, Y. Song, S. Guan, Trans. Nonferrous Met. Soc. China 20, 751 (2010), doi: 10.1016/S1003-6326(09)60209-0
  • [5] R.N. Rao, S. Das, Mater. Des. 31, 1200 (2010), doi: 10.1016/j.matdes.2009.09.032
  • [6] A.M. Al-Qutub, I.M. Allam, M.A.A. Samad, J. Mater. Sci. 43, 5797 (2008), doi: 10.1007/s10853-008-2867-8
  • [7] K.H.W. Seah, J. Hemanth, S.C. Sharma, Mater. Des. 24, 87 (2003), doi: 10.1016/S0261-3069(02)00144-9
  • [8] C.S. Ramesh, R. Keshavamurthy, Mater. Des. 32, 1833 (2011), doi: 10.1016/j.matdes.2010.12.024
  • [9] B.A. Kumar, N. Murugan, Mater. Des. 40, 52 (2012), doi: 10.1016/j.matdes.2012.03.038
  • [10] I. Dinaharan, N. Murugan, Trans. Nonferrous Met. Soc. China 22, 810 (2012), doi: 10.1016/S1003-6326(11)61249-1
  • [11] S. Kumar, M. Chakraborty, V.S. Sarma, B.S. Murty, Wear 265, 134 (2008), doi: 10.1016/j.wear.2007.09.007
  • [12] F. Tag, X. Wu, S. Ge, J. Ye, H. Zhu, M. Hagiwara, J.M. Schoenung, Wear 264, 555 (2008), doi: 10.1016/j.wear.2007.04.006
  • [13] S. Gopalakrishnan, N. Murugan, Composites Part B 43, 302 (2012), doi: 10.1016/j.compositesb.2011.08.049
  • [14] K. Uenishi, T. Matsubara, M. Kambara, K.F. Kobayashi, Scr. Mater. 44, 2093 (2001)
  • [15] D. Özyürek, T. Tuncay, H. Evlen, İ. Çiftçi, Mater. Res. 18, 813 (2015)
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv131n142kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.