2017 | 131 | 1 | 102-105
Article title

An Investigation of Microstructure and Mechanical Properties of Sn-9Zn-xCr Alloys Produced by Investment Casting Method

Content
Title variants
Languages of publication
EN
Abstracts
EN
In this study, the microstructure and mechanical properties were investigated of different amount Cr (0.1%, 0.5%, 0.9%) added Sn-9Zn eutectic alloys and Weibull statistical analyses were evaluated using ultimate tensile strength. Pure elements (Sn, Zn, Cr) were used for production of alloys and pre-alloying was done and waited in the electrical resistance furnace at 450°C for 1 h to homogenized and poured as ingot in plaster moulds. Then pre-alloyed Sn-9Zn-xCr ingots were melted and poured at 300°C in ceramic moulds prepared investment casting method. As a result of the study, the highest hardness and ultimate tensile strength values were measured in the Sn-9Zn alloy with 0.1% Cr. It was determined that while ultimate tensile strength was decreased, percentage of elongation was increased by increase of Cr amount. According to the Weibull statistical analyses results, the highest Weibull module was calculated by Sn-9Zn-0.1Cr alloy ultimate tensile strength values.
Keywords
EN
Contributors
author
  • Karabuk University, Technology Faculty, Manufacturing Eng., 78100 Karabuk, Turkey
author
  • Karabuk University, Technology Faculty, Manufacturing Eng., 78100 Karabuk, Turkey
References
  • [1] M. Abtew, G. Selvaduray, Mater. Sci. Eng. 27, 95 (2000), doi: 10.1016/S0927-796X(00)00010-3
  • [2] L.R. Garcia, W.R. Osorio, L.C. Peixoto, A. Garcia, Mater. Character. 61, 212 (2010), doi: 10.1016/j.matchar.2009.11.012
  • [3] R.A. Islam, Y.C. Chan, W. Jillek, S. Islam, Microelectron. J. 37, 705 (2006), doi: 10.1016/j.mejo.2005.12.010
  • [4] R.A. Islam, B.Y. Wu, M.O. Alam, Y.C. Chan, W. Jillek, J. Alloys Comp. 392, 149 (2005), doi: 10.1016/j.jallcom.2004.08.079
  • [5] A.A. El-Daly, W.M. Desoky, A.F. Saad, N.A. Mansor, E.H. Lotfy, H.M. Abd-Elmoneim, H. Hashem, Mater. Des. 80, 152 (2015), doi: 10.1016/j.matdes.2015.05.016
  • [6] R. Mahmudi, A. Maraghi, Mater. Sci. Eng. A 599, 180 (2014), doi: 10.1016/j.msea.2014.01.082
  • [7] L. Liu, P. Wu, W. Zhou, Microelectron. Reliab. 54, 259 (2014), doi: 10.1016/j.microrel.2013.10.001
  • [8] H.R. Kotadia, P.D. Howes, S.H. Mannan, Microelectron. Reliab. 54, 1253 (2014), doi: 10.1016/j.microrel.2014.02.025
  • [9] M.F.M. Nazeri, A. Mohamad, Measurement 47, 820 (2014), doi: 10.1016/j.measurement.2013.10.002
  • [10] J.C. Liu, G. Zhang, J.S. Ma, K. Suganuma, J. Alloys Comp. 644, 113 (2015), doi: 10.1016/j.jallcom.2015.04.168
  • [11] M. Liu, W. Yang, Y. Ma, C. Tang, H. Tang, Y. Zhan, Mater. Chem. Phys. 168, 27 (2015), doi: 10.1016/j.matchemphys.2015.10.003
  • [12] L. Zhang, K.N. Tu, Mater. Sci. Eng. R 82, 1 (2014), doi: 10.1016/j.mser.2014.06.001
  • [13] C. Wang, P. Li, Mater. Chem. Phys. 138, 937 (2013), doi: 10.1016/j.matchemphys.2013.01.002
  • [14] M.F.M. Nazeri, A.A. Mohamada, J. Mater. Proc. Technol. 219, 164 (2015), doi: 10.1016/j.jmatprotec.2014.12.018
  • [15] M.F.M. Nazeri, A.B. Ismail, A.A. Mohamad, J. Alloys Comp. 606, 278 (2014), doi: 10.1016/j.jallcom.2014.04.034
  • [16] W.R. Osorio, L.C. Peixoto, L.R. Garcia, N. Mangelick-Noel, A. Garcia, J. Alloys Comp. 572, 97 (2013), doi: 10.1016/j.jallcom.2013.03.234
  • [17] Y. Jing, G. Sheng, G. Zhao, Mater. Des. 52, 92 (2013), doi: 10.1016/j.matdes.2013.05.011
  • [18] A.A. El-Daly, A.E. Hammad, J. Alloys Comp. 505, 793 (2010), doi: 10.1016/j.jallcom.2010.06.142
  • [19] A.A. El-Daly, A.E. Hammad, Mater. Sci. Eng. A 527, 5212 (2010), doi: 10.1016/j.msea.2010.04.078
  • [20] G. Ren, I.J. Wilding, M.N. Collins, J. Alloys Comp. 665, 251 (2016), doi: 10.1016/j.jallcom.2016.01.006
  • [21] M.F.M. Nazeri, A.A. Mohamad, J. Alloys Comp. 661, 516 (2016), doi: 10.1016/j.jallcom.2015.11.184
  • [22] S.K. Das, A. Sharif, Y.C. Chan, N.B. Wong, W.K.C. Yung, J. Alloys Comp. 481, 167 (2009), doi: 10.1016/j.jallcom.2009.03.017
  • [23] X. Chen, A. Hu, M. Li, D. Mao, J. Alloys Comp. 460, 478 (2008), doi: 10.1016/j.jallcom.2007.05.087
  • [24] K. Chen, S.C. Cheng, S. Wu, K.L. Lin, J. Alloys Comp. 416, 98 (2006), doi: 10.1016/j.jallcom.2005.08.034
  • [25] A.K. Gain, Y.C. Chan, A. Sharif, N.B. Wong, W.K.C. Yung, Microelectron. Reliab. 49, 746 (2009), doi: 10.1016/j.microrel.2009.05.004
  • [26] T. Fouzder, A.K. Gain, Y.C. Chan, A. Sharif, W.K.C. Yung, Microelectron. Reliab. 50, 2051 (2010), doi: 10.1016/j.microrel.2010.03.017
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv131n129kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.