Mould Walls Inclination and Dendritic Morphology of CMSX-4 Blades Airfoils

• Authors: J. Krawczyk , W. Bogdanowicz , J. Sieniawski , K. Kubiak
• Languages of publication: EN

Abstracts

EN

The airfoils of single-crystalline turbine blades were studied. The blades made of industrial CMSX-4 superalloy were obtained by the Bridgman technique. Five different withdrawal rates (1-5 mm/min) were used. Series of as-cast samples were prepared by cutting the airfoils at different distances from the blade root. The metallographic sections, prepared for each cutting planes, were subjected to scanning electron microscopy observations and Laue diffraction studies. Macrostructure images of whole area of airfoil cross-sections were obtained by stitching several obtained SEM images. Morphology of dendrites in different area of cross-sections were analysed. The crystal orientation of each sample were determined by analysis of Laue pattern. It was found that the morphology of dendrites changes in the area, where the dendrite growth is limited by inclined mould walls.

Keywords

EN

68.70.+w; 61.66.Dk; 61.72.Bb

Discipline

• 61.72.Bb: Theories and models of crystal defects
• 68.70.+w: Whiskers and dendrites (growth, structure, and nonelectronic properties)
• 61.66.Dk: Alloys

• Publisher: Institute of Physics, Polish Academy of Sciences
• Journal: Acta Physica Polonica A
• Year: 2016
• Volume: 130
• Issue: 4
• Pages: 1100-1103

Dates

published

2016-10

Contributors

author

J. Krawczyk

• Institute of Materials Science, University of Silesia, 75 Pułku Piechoty 1a, 41-500 Chorzów, Poland

author

W. Bogdanowicz

• Institute of Materials Science, University of Silesia, 75 Pułku Piechoty 1a, 41-500 Chorzów, Poland

author

J. Sieniawski

• Department of Materials Science, Rzeszów University of Technology, W. Pola 2, 35-959 Rzeszów, Poland

author

K. Kubiak

• Department of Materials Science, Rzeszów University of Technology, W. Pola 2, 35-959 Rzeszów, Poland

References

• [1] R. Reed, The Superalloys: Fundamentals and Application, Cambridge University Press, Cambridge 2006, doi: 10.1017/CBO9780511541285
• [2] M.J. Donachie, S.J. Donachie, Superalloys. A Technical Guide, ASM International, Ohio 2002
• [3] A. Wawrzyniak, M. Wieczorek, T. Ryniewicz, Przegląd mechaniczny 12, 14 (2012) (in Polish)
• [4] J.W. Aveson, G. Reinhart, H. Nguyen-Thi, N. Mangelinck-Noël, A. Tandjaoui, B. Billia, K. Goodwin, T.A. Lafford, J. Baruchel, H.J. Stone, N. D'Souza, in: Superalloys 2012, Eds. E.S. Huron, R.C. Reed, M.C. Hardy, M.J. Mills, R.E. Montero, P.D. Portella, J. Telesman, TMS, 2012, p. 615
• [5] E. Rzyankina, D. Szeliga, N. Mahomed, A. Nowotnik, Appl. Mech. Mater. 372, 54 (2013), doi: 10.4028/www.scientific.net/AMM.372.54
• [6] A. Onyszko, W. Bogdanowicz, K. Kubiak, J. Sieniawski, Cryst. Res. Technol. 45, 1326 (2010), doi: 10.1002/crat.201000389

Identifiers

DOI

10.12693/APhysPolA.130.1100