Analysis of Phase Transformations in Inconel 625 Alloy during Annealing

• Authors: P. Petrzak , K. Kowalski , M. Blicharski
• Languages of publication: EN

Abstracts

EN

The investigation focused on the characterization of the microstructure and chemical composition changes after annealing. The research was conducted on the Inconel 625 weld overlay deposited on a boiler steel. The annealing was performed for 10 h at temperatures from 600 to 1000°C. The microstructure and chemical composition were examined by scanning electron microscope and transmission electron microscope equipped with an energy dispersive X-ray spectrometer. Weld overlays were produced by an innovative method of cold metal transfer.

Keywords

EN

61.66.Dk   64.75.Nx   81.05.Bx   81.30.Fb  

• Publisher: Institute of Physics, Polish Academy of Sciences
• Journal: Acta Physica Polonica A
• Year: 2016
• Volume: 130
• Issue: 4
• Pages: 1041-1044

Dates

published

2016-10

References

• [1] J.N. DuPont, J.C. Lippold, S.D. Kiser, Welding Metallurgy and Weldability of Nickel-Base Alloys, Wiley, New Jersey 2009
• [2] B. Mikułowski, Heat and creep resistant alloys, Wyd. AGH, Kraków 1997
• [3] B. Dubiel, Changes in microstructure during creep monocrystalline nickel superalloys, monograph, 2011
• [4] E. Gozlan, M. Bamberger, S.F. Dirnfeld, B. Prinz, J. Klodt, Mater. Sci. Eng. A 141, 85 (1991), doi: 10.1016/0921-5093(91)90712-V
• [5] A. Hernas, Creep resistant steels and alloys, Wydawnictwo Politechniki Śląskiej, Gliwice 1999
• [6] X. Xing, X. Di, B. Wang, J. Alloys Comp. 593, 110 (2014), doi: 10.1016/j.jallcom.2013.12.224
• [7] M. Rozmus-Górnikowska, M. Blicharski, J. Kusiński, L. Kusiński, M. Marszycki, Archiv. Metall. Mater. 58, 1093 (2013), doi: 10.2478/amm-2013-0131
• [8] J. Adamiec, Mater. Charact. 60, 1093 (2009), doi: 10.1016/j.matchar.2009.03.017
• [9] J.N. DuPont, Metall. Mater. Trans. A 27, 3612 (1996)
• [10] V. Shankar, K. Bhanu Sankara Rao, S.L. Mannan, J. Nucl. Mater. 288, 222 (2001), doi: 10.1016/S0022-3115(00)00723-6
• [11] S.W. Banovic, J.N. DuPont, A.R. Marder, Sci. Technol. Weld. Joining 7, 374 (2002), doi: 10.1179/10.1179/136217102225006804
• [12] Q. Guo, D. Li, H. Peng, S. Guo, J. Hu, P. Du, Rare Met. 31, 215 (2012), doi: 10.1007/s12598-012-0494-7
• [13] H.M. Tawancy, N.M. Allam, J. Mater. Sci. Lett. 9, 343 (1990)
• [14] Fronius International [access: 1 November 2015] http://www.fronius.com/cps/rde/xchg/fronius_international/hs.xsl/79_9399_ENG_HTML.htm
• [15] C.G. Pickin, S.W. Williams, M. Lunt, J. Mater. Process. Technol. 211, 496 (2011), doi: 10.1016/j.jmatprotec.2010.11.005

Identifiers

DOI

10.12693/APhysPolA.130.1041