Journal
Article title
Authors
Title variants
Languages of publication
Abstracts
In this work, we have intended to synthesize ZE41 Magnesium alloys having varying content of Ce of 0.3, 0.6 and 0.9 wt.% and to investigate mechanical properties of these alloys. Alloys were produced by mechanical alloying under argon atmosphere. Structural, and mechanical properties of these alloys were investigated by means of XRD, SEM and nanoindenter analysis. From the XRD data it is found that as the Ce content increases, the crystallite size also increases. On the other hand, the hardness of the alloys decreases with the increasing Ce content. Indentation results show that the measured hardness displays a peak load dependence. Load-independent hardness was calculated by Hays-Kendall approach. As a results, it was found that Ce-doping modifies the microstructure and hardness of the alloy.
Discipline
Journal
Year
Volume
Issue
Pages
289-292
Physical description
Dates
published
2016-07
Contributors
author
- Mustafa Kemal University, Science and Art Faculty, Micro/Nanomechanic Characterization Laboratory, Hatay 31034, Turkey
author
- Mustafa Kemal University, Science and Art Faculty, Micro/Nanomechanic Characterization Laboratory, Hatay 31034, Turkey
author
- Mustafa Kemal University, Science and Art Faculty, Micro/Nanomechanic Characterization Laboratory, Hatay 31034, Turkey
author
- Mustafa Kemal University, Science and Art Faculty, Micro/Nanomechanic Characterization Laboratory, Hatay 31034, Turkey
References
- [1] F.H. Froes, D. Eliezer, E. Aghion, JOM 50, 30 (1998), doi: 10.1007/s11837-998-0411-6
- [2] M. Gupta, N.M.L. Sharon, Magnesium Alloys and Magnesium Composites, John Wiley & Sons, New Jersy 2011
- [3] G.I. Rosen, G. Segal, A. Lubinsky, Materials Sci. Forum 488-489, 509 (2005), doi: 10.4028/www.scientific.net/MSF.488-489.509
- [4] C. Suryanarayana, Prog. Mater. Sci. 46, 1 (2001), doi: 10.1016/S0079-6425(99)00010-9
- [5] C. Suryanarayana, in: Powder metal technologies and applications. ASM Handbook, ASM International, Materials Park 1998, Vol. 7., p. 80
- [6] M.L.B. Palacio, B. Bhushan, Mater. Charact. 78, 1 (2013), doi: 10.1016/j.matchar.2013.01.009
- [7] S. Lee, B.G. Choi, D. Choi, H.S. Park, J. Membr. Sci. 451, 40 (2014), doi: 10.1016/j.memsci.2013.09.038
- [8] S.R. Jian, G.J. Chen, W.M. Hsu, Materials 6, 4505 (2013), doi: 10.3390/ma6104505
- [9] S.R. Jian, Y.Y. Lin, W.C. Ke, Sci. Adv. Mater. 5, 7 (2013), doi: 10.1166/sam.2013.1424
- [10] S.R. Jian, Y.H. Lee, J. Alloy. Compd. 587, 313 (2014), doi: 10.1016/j.jallcom.2013.10.213
- [11] A.E. Ozmetin, O. Sahin, E. Ongun, M. Kuru, J. Alloy. Compd. 619, 262 (2015), doi: 10.1016/j.jallcom.2014.09.015
- [12] W.C. Oliver, G.M. Pharr, J. Mater. Res. 7, 1564 (1992), doi: 10.1557/JMR.1992.1564
- [13] O. Sahin, O. Uzun, M. Sopicka-Lizer, H. Gocmez, U. Kolemen, J. Phys. D: Appl. Phys. 41, 035305 (2008), doi: 10.1088/0022-3727/41/3/035305
- [14] F. Haluk Ertsak, M.Sc. Thesis, Mustafa Kemal University, 2015
- [15] O. Sahin, İ. Demirkol, H. Göcmez, M. Tuncer, H. Ali Cetinkara, H. Salih Güder, E. Sahin, A. Rıza Tuncdemir, Acta Phys. Pol. 123, 296 (2013), doi: 10.12693/APhysPolA.123.296
- [16] C. Hays, E.G. Kendall, Metallography 6, 275 (1973), doi: 10.1016/0026-0800(73)90053-0
- [17] O. Şahin, O. Uzun, U. Kölemen, N. Uçar, Material Characterization 59, 729 (2008), doi: 10.1016/j.matchar.2007.06.005
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv130n1075kz