Fabrication and Characterisation of Bronze Pads and Comparison with Commercial Bronze Pads

Authors
Content
Title variants
Languages of publication
EN
Abstracts
EN
CuSn10 pre-alloyed bronze with iron and graphite powders were mixed, pressed and sintered for the bronze pad fabrication. The powder mix was pressed under pressure in the range of 100-600 MPa and sintered at temperatures between 780-850°C. The optimum compression was at 500 MPa and the optimal sintering temperatures was 730°C. 2 wt.% of graphite addition was sufficient to adjust the friction and wear properties of produced bronze pad samples. Optical microscope and SEM images showed that a homogenous powder mix was achieved. The produced bronze samples and the commercial ones were compared and beneficial properties of them were determined. The wear behaviours of both the produced friction materials and the commercial pads were examined. The coefficient of friction and wear rates were determined. The sintered bronze samples and the commercial bronze pads have exhibited similar wear behaviour, although the commercial one have contained ceramic particles.
Keywords
EN
Contributors
author
  • Faculty of Technology, Department of Metallurgical and Materials Engineering, Sakarya University, Serdivan, Sakarya, Turkey
References
  • [1] W. Ma, J. Lu, B. Wang, Wear 266, 1072 (2009), doi: 10.1016/j.wear.2009.01.051
  • [2] R. Junghans, J. Neukirchner, D. Schumann, K.H. Lippman, Tribol. Int. 29, 181 (1996), doi: 10.1016/0301-679X(95)00087-K
  • [3] S.F. Moustafa, S.A. El-Badry, A.M. Sanad, B. Kieback, Wear 253, 699 (2002), doi: 10.1016/S0043-1648(02)00038-8
  • [4] J. Jun-Hong, C. Jian-Min, Z. Hui-Di, W. Jing-Bo, Z. Hua, Tribol. Int. 37, 423 (2004), doi: 10.1016/j.triboint.2003.12.013
  • [5] C.G. Clarke, C. Allen. Tribol. Int. 24, 109 (1991), doi: 10.1016/0301-679X(91)90041-7
  • [6] S.F Moustafa S.A. El-Badry, A.M. Sanad, Powder Metall. 40, 201 (1997), doi: 10.1179/pom.1997.40.3.201
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv129n4122kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.