An Investigation of the Effects of Ageing Parameters on Wear Behaviours and Electrical Conductivity of Cu-Co-Be Alloys

• Authors: D. Özyürek , M. Yıldırım , T. Tunçay
• Languages of publication: EN

Abstracts

EN

In this study, the effects of ageing parameters were investigated on wear behaviours and electrical conductivity of Cu-Co-Be alloy. The samples were quenched at room temperature after solution heat treated for 1 h. Then, ageing processes were applied for three different temperatures (470°C, 500°C, 530°C) and for three different ageing times (1, 2, 3 h). Microstructure examining, electrical conductivity and hardness measurements were carried out after ageing process. On the samples, which obtained the highest hardness values from hardness test (470°C), there were carried out wear tests with 1 m s¯¹ sliding speed under 30 N at four sliding distance (500-2000 m). Results clearly show that the highest hardness values were measured for samples aged at 470°C for 3 h and hardness values were decreased with increasing ageing temperature. The lowest weight loss values were evaluated for samples aged at 470°C for 3 h. The highest electrical conductivity values were measured at 500°C for 1 h aged samples.

Keywords

EN

81.40.Pq

Discipline

• 81.40.Pq: Friction, lubrication, and wear

• Publisher: Institute of Physics, Polish Academy of Sciences
• Journal: Acta Physica Polonica A
• Year: 2016
• Volume: 129
• Issue: 4
• Pages: 559-561

Dates

published

2016-04

Contributors

author

D. Özyürek

• Karabük University, Technology Faculty, Department of Manufacturing Engineering, Karabük, Turkey

author

M. Yıldırım

• Karabük University, Technology Faculty, Department of Manufacturing Engineering, Karabük, Turkey

author

T. Tunçay

• Karabük University, Technology Faculty, Department of Manufacturing Engineering, Karabük, Turkey

References

• [1] H. Fuxiang, L. Chao, M. Jusheng, N. Honglong, G. Zhiting, L. Chao, G. Shumei, Y. Xuetao, W. Tao, L. Hong, L. Huafen, Scr. Mater. 48, 97 (2003)
• [2] Q. Liu, X. Zhang, Zhang, Y. Ge, J. Wang, J.Z. Cui, Metall. Trans. A 37A, 3233 (2006)
• [3] X. Guoliang, W. Qiangsong, M. Xujun, X. Baiqing, P. Lijun, Mater. Sci. Eng. 558, 326 (2012), doi: 10.1016/j.msea.2012.08.007
• [4] P. Scardi, M. Leoni, G. Straffelini, G. De Giudici, Acta Mater. 55, 2531 (2007), doi: 10.1016/j.actamat.2006.11.046
• [5] L. Yağmur, O. Duygulu, B. Aydemir, Mater. Sci. Eng. A 528, 4147 (2011), doi: 10.1016/j.msea.2011.01.114
• [6] H.B. Yıldız, M. Yaşar, Metallofiz. Noveishie Tekhnol. 29, 1659 (2007)
• [7] D. Özyürek, İ. Çiftci, T. Tuncay, Mater. Test. 55, 468 (2013), doi: 10.3139/120.110457
• [8] İ. Sağlam, D. Özyürek, K. Çetinkaya, Bull. Mater. Sci. 34, 1465 (2011)
• [9] Y. Altunpak, Sci. Res. Essays 5, 2997 (2010)

Identifiers

DOI

10.12693/APhysPolA.129.559