Investigation of Wear Behavior of Precipitation-Strengthened Nickel-Copper Based K-500 Alloy Produced by Powder Metallurgy

Content
Title variants
Languages of publication
EN
Abstracts
EN
The present study investigates the effects of the ageing parameters of the precipitation-strengthened nickel-copper based K-500 alloy produced by powder metallurgy on the wear behavior of the alloy. After the cold pressing the prepared alloy powders under 600 MPa pressure, the samples were sintered under vacuum (10¯⁶ mbar) at 1150°C for 2 h and then cooled in the furnace. Produced K-500 alloy samples were taken into solution at 980°C for 1 h and quenched. Ageing process was carried out at 480°C for four different time periods (6, 8, 10, and 12 h). Aged samples were examined transmission electron microscope (TEM + EDS), X-ray diffraction (XRD), hardness and density measurements. The wear tests were carried out at 1 ms¯¹ constant sliding speed, under 40 N load and for five different sliding distances (400-2000 m). The results showed that there is γ' Ni₃(Al, Ti) inter-metallic phase coexisting with Al_{0.9}Ni_{4.22}, AlNi₃ and NiO phases. According to the hardness measurements, the highest hardness values were obtained with samples aged for 8 h. In wear tests with 2000 m sliding distance, the lowest weight loss was observed for the samples aged for 8 h.
Keywords
EN
Publisher

Year
Volume
129
Issue
4
Pages
544-547
Physical description
Dates
published
2016-04
Contributors
author
  • Karabuk University, Technology Faculty, Department of Manufacturing Engineering, 78050 Karabuk, Turkey
author
  • Karabuk University, Technology Faculty, Department of Manufacturing Engineering, 78050 Karabuk, Turkey
author
  • Kocaeli University, Asim Kocabiyik Vocational School of Higher Education, Department of Machine, 41800 Kocaeli, Turkey
References
  • [1] B. Chen, J. Wang, F. Yan, Tribol. Lett. 42, 17 (2011), doi: 10.1007/s11249-010-9743-9
  • [2] R.J.K. Wood, Wear 261, 1012 (2006), doi: 10.1016/j.wear.2006.03.033
  • [3] N. Espallargas, S. Mischler, Tribol. Int. 43, 1209 (2010), doi: 10.1016%2fj.triboint.2009.12.009
  • [4] K.C. Tekin, U. Malayoglu, Tribol. Lett. 37, 563 (2010), doi: 10.1007/s11249-009-9552-1
  • [5] A. Yano, A. Sakanishi, F. Takahashi, S. Shirai, Y. Uchida, K. Fujita, F. Kikkawa, K. Fujioka, T. Kawazoe, K. Saki, Y. Yamamoto, Tribol. Trans. 50, 13 (2007), doi: 10.1080/10402000600927928
  • [6] E. Boese, J. Rothig, I. Garz, H. Schmidtchen, Mater. Corros. 49, 98 (1998), doi: 10.1002/(SICI)1521-4176(199802)49:2%3C98::AID-MACO98%3E3.3.CO;2-Z
  • [7] S.W. Watson, F.J. Friedersdorf, B.W. Madsen, S.D. Cramer, Wear 181, 476 (1995), doi: 10.1016/0043-1648(95)90161-2
  • [8] A.G. Evgenov, V.A. Kalitsev, A.M. Rogalev, Metallurgist 57, 736 (2013), doi: 10.1007/s11015-013-9794-x
  • [9] L.E. Shoesmaker, G.D. Simith, JOM 58, 22 (2006), doi: 10.1007/s11837-006-0077-x
  • [10] A.G. Evgenov, G.I. Morozova, V.I. Lukin, Met. Sci. Heat Treat. 48, 364 (2006), doi: 10.1016/S1350-6307(99)00031-X
  • [11] O.S. Es-Said, K. Zakharia, Z. Zakharia, C. Ventura, D. Pfost, P. Crawford, T. Ward, D. Raizk, J. Foyos, R. Marloth, Eng. Fail. Anal. 7, 323 (2000), doi: 10.1016/S1350-6307(99)00031-X
  • [12] G.K. Dey, P. Mukhopadhyay, Mater. Sci. Eng. 84, 177 (1986), doi: 10.1016/0025-5416(86)90236-3
  • [13] G.K. Dey, R. Tewari, P. Rao, S.L. Wadekar, P. Mukhopadhyay, Metall. Trans. A 24, 2709 (1993), doi: 10.1007/BF02659495
  • [14] J.H. Ai, H.M. Ha, R.P. Gangloff, J.R. Scully, Acta Mater. 61, 3186 (2013), doi: 10.1016/j.actamat.2013.02.007
  • [15] I. Saglam, D. Özyürek, K. Cetinkaya, Bull. Mater. Sci. 34, 1465 (2011), doi: 10.1007/s12034-011-0344-5
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv129n4032kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.