The surface treatment of volcanic ash particles with various concentrations (1-3-5% (v/v)) silane coupling agent (3-aminopropyltriethoxysilane (3-APTS)) having organic functional group was conducted. After surface treatment, polyphenylene sulfide (PPS) composite samples containing surface treated volcanic ash particles at two concentrations (10 and 15 wt%) were manufactured by twin screw extruder and injection molding machine. This study investigated the effect of surface modification on mechanical properties of two different concentrated volcanic ash/PPS composites. All tests were performed using a Shimadzu AG-X Universal Tester. Tensile and three point bending tests were carried out at a crosshead speed of 1 mm/min and 2 mm/min according to ISO 527-2 and ASTM D790 standards, respectively. During the experiments, the relation between the mechanical properties and surface treatment concentrations of silane agent on volcanic ash/PPS composites was determined as a function of tensile strength and modulus, flexural strength and modulus. Moreover, fracture surface morphologies of volcanic ash/PPS composite samples were observed by using a scanning electron microscopy.
Keywords
Journal
Year
Volume
Issue
Pages
495-497
Physical description
Dates
published
2016-04
Contributors
author
- Kocaeli University, Faculty of Aeronautics and Astronautics, 41285, Kartepe-Kocaeli, Turkey
author
- Kocaeli University, Faculty of Aeronautics and Astronautics, 41285, Kartepe-Kocaeli, Turkey
author
- Kocaeli University, Faculty of Aeronautics and Astronautics, 41285, Kartepe-Kocaeli, Turkey
author
- Kocaeli University, Department of Chemical Engineering, 41380, Umuttepe-Kocaeli, Turkey
author
- Kocaeli University, Department of Mechanical Engineering, 41380, Umuttepe-Kocaeli, Turkey
References
- [1] C.J. Schwartz, S. Bahadur, Wear 237, 261 (2000), doi: 10.1016/S0043-1648(99)00345-2
- [2] Y. Yang, H. Duan, S. Zhang, P. Niu, G. Zhang, S. Long, X. Wang, J. Yang, Compos. Sci. Technol. 75, 28 (2013), doi: 10.1016/j.compscitech.2012.11.006
- [3] S.G. Pardo, C. Bernal, M.J. Abad, J. Cano, L.B. Losada, Compos. Interface 16, 97 (2009), doi: 10.1163/156855408X402830
- [4] P.N. Lemougna, U.F.C. Melo, M.P. Delplancke, H. Rahier, Ceram. Int. 40, 811 (2014), doi: 10.1016/j.ceramint.2013.06.072
- [5] E. Avcu, O. Çoban, M.Ö. Bora, S. Fidan, T. Sınmazçelik, O. Ersoy, Polym. Compos. 35, 1826 (2014), doi: 10.1002/pc.22847
- [6] J. Pionteck, V.B. Sadhu, L. Jakisch, P. Pötschke, L. Häubler, A. Janke, Polymer 46, 6563 (2005), doi: 10.1016/j.polymer.2005.05.010
- [7] S. Thongsang, N. Sombatsompop, Polym. Compos. 27, 30 (2005), doi: 10.1002/pc.20163
- [8] D.S. Chaudhary, M.C. Jollands, F. Cser, Adv. Polym. Tech. 23, 147 (2004), doi: 10.1002/adv.20000
- [9] Ticona, 2014. Information on http://tools.ticona.com/tools/mcbasei/product-tools.php?sPolymer=&sProduct=,(10.03.2015)
- [10] A.G.S. Prado, C. Airoldi, Pest. Manag. Sci. 56, 419 (2000), doi: 10.1002/(SICI)1526-4998(200005)56:5<419::AID-PS142>3.0.CO;2-7
- [11] DSM, 2014. Information on http://www.xplore-together.com/15ml_compounder.htm., (12.03.2015)
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv129n4018kz