In the present work, the influence of annealing conditions on magnetic properties and phase constitution of the rapidly solidified Fe₆₅Pr₉B₁₈W₈ alloy ribbons, were investigate. Samples were prepared by arc-melting of high purity constituent elements under the Ar atmosphere. Ribbons were obtained by melt-spinning technique under low pressure of Ar. The ribbons in as-cast state had amorphous structure and soft magnetic properties. Heat treatment, carried out at various temperatures (from 923 K to 1023 K) for 5 min, resulted in an evolution of the phase constitution that caused changes in magnetic properties of the alloy. The crystallization behavior was studied using differential scanning calorimetry and X-ray diffractometry. The room temperature magnetic properties were determined from hysteresis loops measured by VSM magnetometer in the external magnetic field up to 2 T.
Discipline
Journal
Year
Volume
Issue
Pages
185-187
Physical description
Dates
published
2016-02
Contributors
author
- Institute of Physics, Faculty of Production Engineering and Materials Technology, Częstochowa University of Technology, al. Armii Krajowej 19, 42-200 Częstochowa, Poland
- Institute of Physics, Faculty of Mathematics and Natural Science, Jan Długosz University, al. Armii Krajowej 13/15, 42-200 Częstochowa, Poland
author
- Institute of Physics, Faculty of Production Engineering and Materials Technology, Częstochowa University of Technology, al. Armii Krajowej 19, 42-200 Częstochowa, Poland
author
- Department of Physics, Faculty of Production Engineering and Logistics, Opole University of Technology, Ozimska 75, 45-370 Opole, Poland
author
- Institute of Physics, Faculty of Mathematics and Natural Science, Jan Długosz University, al. Armii Krajowej 13/15, 42-200 Częstochowa, Poland
References
- [1] J.J. Croat, J.F. Herbst, R.E. Lee, F.E. Pinkerton, J. Appl. Phys. 55, 2078 (1984), doi: 10.1063/1.333571
- [2] M. Sagawa, S. Fujimura, N. Togawa, H. Yamamoto, J. Appl. Phys. 55, 2083 (1984), doi: 10.1063/1.333572
- [3] R. Skomski, J.M.D. Coey, Permanent Magnetism, Taylor & Francis Group, New York 1999
- [4] D. Givord, H.S. Li, R. Perrier de la Bathie, Solid State Commun. 51, 857 (1984), doi: 10.1016/0038-1098(84)91087
- [5] E.B. Boltich, E. Oswald, M.Q. Haung, S. Hirosawa, J. Appl. Phys. 57, 4106 (1985), doi: 10.1063/1.33463
- [6] S. Hirosawa, Y. Matsuura, H. Yamamoto, J. Appl. Phys. 59, 873 (1986), doi: 10.1063/1.33661
- [7] D.H. Ping, T.S. Xie, D.X. Li, H.Q. Ye, Nanostruct. Mater. 5, 457 (1995), doi: 10.1016/0965-9773(95)00259-H
- [8] J.F. Herbst, J.J. Croat, J. Magn. Magn. Mater. 100, 57 (1991), doi: 10.1016/0304-8853(91)90812-O
- [9] P. Pawlik, H.A. Davies, Scr. Mater. 49, 755 (2003), doi: 10.1016/S1359-6462(03)00428-7
- [10] H.W. Chang, C.H. Chiu, C.W. Chang, C.H. Chen, W.C. Chang, Y.D. Yao, A.C. Sun, J. Alloys Comp. 407, 53 (2006), doi: 10.1016/j.jallcom.2005.06.040
- [11] P. Pawlik, K. Pawlik, J.J. Wysłocki, W. Kaszuwara, J. Ferenc, J. Alloys Comp. 536, S342 (2011), doi: 10.1016/j.jallcom.2011.12.005
- [12] A.D. Barra-Barrera, A.M. Pizzo, V. Villas-Boas, J. Magn. Magn. Mater. 302, 68 (2006), doi: 10.1016/j.jmmm.2005.08.024
- [13] K. Filipecka, K. Pawlik, P. Pawlik, J.J. Wysłocki, P. Gebara, A. Przybył, Acta Phys. Pol. A 126, 164 (2014), doi: 10.12693/APhysPolA.126.164
- [14] A. Przybył, J.J. Wysłocki, J. Mater. Process. Technol. 175, 352 (2006), doi: 10.1016/j.jmatprotec.2005.04.064
- [15] K. Pawlik, EPJ Web Conf. 40, 06004 (2013), doi: 10.1051/epjconf/20134006004
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv129n206kz