2015 | 128 | 4 | 726-729
Article title

Characterization of Hot Deformation of CW602N Brass

Content
Title variants
Languages of publication
EN
Abstracts
EN
Alpha brasses (in principle single-phase solid solution alloys containing less than 35% Zn) are usually processed by extrusion, forging or rolling. Although these materials are of widespread use, few detailed studies of the flow behavior of brass at high temperature are available. The hot workability of a CW602N brass (Cu-36.5%Zn-2%Pb) was thus investigated by torsion testing in the temperature range between 550 and 800°C, under equivalent strain rates ranging from 0.01 to 10 s^{-1}. The peak flow stress dependence on temperature and strain rate was described by the well-known Garofalo equation, with a stress exponent close to 4 and Q=220 kJ mol^{-1}. A considerably larger scatter of the experimental data was observed in the high temperature range. The detailed microstructural analysis of the deformed samples by scanning electron microscopy revealed substantial differences among the samples deformed in the low temperature regime and those torsioned at 750 and 800°C. These differences were analyzed and discussed to rationalize the different mechanical responses observed in the two hot-deformation regimes.
Keywords
Contributors
author
  • DIISM, Università Politecnica delle Marche, via Brecce Bianche 60131 Ancona, Italy
author
  • DIISM, Università Politecnica delle Marche, via Brecce Bianche 60131 Ancona, Italy
author
  • DIISM, Università Politecnica delle Marche, via Brecce Bianche 60131 Ancona, Italy
References
  • [1] J.R. Cho, H.S. Jeong, D.J. Cha, W.B. Bae, J.W. Lee, J. Mater. Proc. Tech. 160, 1 (2005), doi: 10.1016/j.jmatprotec.2004.01.001
  • [2] R.M. Bonesteel, O.D. Sherby, Acta Metall. 14, 385 (1966), doi: 10.1016/0001-6160(66)90096-4
  • [3] S.A. Mahmoud, M.A. Semary, Z.M. Farid, N. El-Naquib, Mater. Sci. Eng. A 118, 107 (1989), doi: 10.1016/0921-5093(89)90062-2
  • [4] S.V. Raj, J. Mater. Sci. 26, 3533 (1991), doi: 10.1007/BF00557142
  • [5] R. Pernis, J. Kasala, J. Boruta, Kovove Mater. 48, 41 (2010), doi: 10.4149/km_2010_1_41
  • [6] M. Suery, B. Baudelet, J. Mater. Sci. 8, 363 (1973), doi: 10.1007/BF00550156
  • [7] J.W.D. Patterson, N. Ridley, J. Mater. Sci. 16, 457 (1981), doi: 10.1007/BF00738637
  • [8] D. Hua, W. Qingling, M. Lonxiang, J. Mater. Sci. 27, 607 (1992), doi: 10.1007/BF00554024
  • [9] K. Neishi, Z. Horita, T.G. Langdon, Scr. Mater. 45, 965 (2001), doi: 10.1016/S1359-6462(01)01119-8
  • [10] T. Chandra, J.J. Jonas, D.M.R. Taplin, J. Mater. Sci. 13, 2380 (1978), doi: 10.1007/BF00808052
  • [11] H. Miyamoto, T. Tanaka, T. Mimaki, R. Matsubara, N. Ashie, S. Miura, Mater. Sci. Eng. A 380, 34 (2004), doi: 10.1016/j.msea.2004.03.048
  • [12] Y.-H. Xiao, C. Guo, X.-Y. Guo, Mater. Sci. Eng. A 528, 6510 (2011), doi: 10.1016/j.msea.2011.04.090
  • [13] D. Padmavardhani, Y.V.R.K. Prasad, Metall. Trans. 22A, 2993 (1991), doi: 10.1007/BF02650259
  • [14] B.L. Vaandrager, G.M. Pharr, Scr. Metall. 18, 1337 (1984), doi: 10.1016/0036-9748(84)90134-0
  • [15] A.P. Miodownik, in: ASM Handbook, Vol. 3, 1987, p. 2
  • [16] V. Buršiková, J. Buršik, V. Navrátil, K. Milička, Mater. Sci. Eng. A 324, 235 (2002), doi: 10.1016/S0921-5093(01)01317-X
  • [17] K.J. Anusavice, R.T. DeHoff, Metall. Trans. 3, 1279 (1972), doi: 10.1007/BF02642463
  • [18] R. Fuentes-Samaniego, W.D. Nix, Scr. Metall. 15, 15 (1981), doi: 10.1016/0036-9748(81)90129-0
  • [19] R. Fuentes-Samaniego, W.D. Nix, G.M. Pound, Acta Metall. 29, 487 (1981), doi: 10.1016/0001-6160(81)90072-9
  • [20] S. Spigarelli, M. El Mehtedi, M. Cabibbo, F. Gabrielli, D. Ciccarelli, Mater. Sci. Eng. A 615, 331 (2014), doi: 10.1016/j.msea.2014.07.091
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv128n462kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.