2015 | 128 | 3 | 377-382
Article title

The Effect of Milling Time and Sintering Temperature on Crystallization of BaFe₁₂O₁₉ Phase and Magnetic Properties of Ba-Hexaferrite Magnet

Content
Title variants
Languages of publication
EN
Abstracts
EN
Barium hexaferrite samples were prepared by mechanical alloying using the stoichiometric amounts of BaCO₃ and Fe₂O₃ precursors followed by heat treatment applied in the temperature range 700-1150°C. It was found that the high energy ball mill with a milling rate enabled to obtain powders with the finer particles at the reduced milling time mechanical alloying of the initial powders linked to the formation of barium hexaferrite phase. The exothermic reaction peaks corresponding to the formation of BaFe₁₂O₁₉ phase shift from 928°C to 793°C for the increased milling time up to 6 h. This was resulted in improved magnetic properties that the Mₛ value of the as-blended sample sintered at 800°C rised from 31.16 emu/g to 53.46 emu/g after milling for 6 h. The saturation magnetization and remanence values of the samples mechanically alloyed for 3 h and sintered at 1150°C also increased to 63.57 emu/g and 31.26 emu/g, respectively, more than for 800°C and 900°C. The increase in the annealing temperature favours the formation of BaFe₁₂O₁₉ phase in the samples.
Keywords
EN
Year
Volume
128
Issue
3
Pages
377-382
Physical description
Dates
published
2015-09
received
2014-04-02
(unknown)
2015-06-15
References
  • [1] B.D. Cullity, C.D. Graham, Introduction to Magnetic Materials, Wiley, New Jersey, USA 2009, p. 190
  • [2] R. Smomski, J.M.D. Coey, Permanent Magnetism, Bookcraft, UK 1999, p. 261
  • [3] A. Goldman, Modern Ferrite Technology, 2nd ed., Springer, New York 2006, p. 104
  • [4] S.B. Narang, I.S. Hudiara, J. Ceram. Process. Res. 7, 113 (2006)
  • [5] K.K. Mallick, P. Shepherd, R.J. Green, J. Europ. Ceram. Soc. 27, 2045 (2007), doi: 10.1016/j.jeurceramsoc.2006.05.098
  • [6] J. Bursik, Z. Simsa, M. Cernansky, J. Sol-Gel Sci. Technol. 8, 947 (1997), doi: 10.1007/BF02436966
  • [7] S. Hussain, A. Maqsood, J. Magn. Magn. Mater. 316, 73 (2007), doi: 10.1016/j.jmmm.2007.03.206
  • [8] S.R. Janasi, M. Emura, F.J.G. Landgraf, D. Rodrigues, J. Magn. Magn. Mater. 238, 168 (2002), doi: 10.1016/S0304-8853(01)00857-5
  • [9] M. El-Hilo, H. Pfeiffer, K. O'Grady, W. Schüppel, E. Sinn, P. Görnert, M. Rösler, D.P.E. Dickson, R.W. Chantrell, J. Magn. Magn. Mater. 129, 339 (1994), doi: 10.1016/0304-8853(94)90130-9
  • [10] O. Abe, M. Narita, Solid State Ion. 101, 103 (1997), doi: 10.1016/S0167-2738(97)84016-7
  • [11] A. Gonzales-Angeles, G. Mendoza-Suarez, A. Gruskova, R. Dosoudil, R. Ortega Zempoalteca, Mater. Lett. 58, 2906 (2004), doi: 10.1016/j.matlet.2004.05.017
  • [12] S. Wang, J. Ding, Y. Shi, Y.J. Chen, J. Magn. Magn. Mater. 219, 206 (2000), doi: 10.1016/S0304-8853(00)00450-9
  • [13] J. Ding, D. Maurice, W.F. Miao, P.G. McCormick, R. Street, R. Street, J. Magn. Magn. Mater. 150, 417 (1997), doi: 10.1016/0304-8853(95)00279-0
  • [14] J. Ding, H. Yang, W.F. Miao, P.G. McCormick, R. Street, R. Street, J. Alloys Comp. 221, 70 (1995), doi: 10.1016/0925-8388(94)01402-7
  • [15] P. Sharma, R.A. Rocha, S.N. de Medeiros, A. Paesano Jr., J. Alloys Comp. 443, 37 (2007), doi: 10.1016/j.jallcom.2006.10.022
  • [16] D. Lisjak, M. Drofenik, J. Europ. Ceram. Soc. 24, 1841 (2004), doi: 10.1016/S0955-2219(03)00445-X
  • [17] Powder Diffraction Files: Card No. 41-0373, database edition, The International Center for Diffraction Data (ICDD)
  • [18] Powder Diffraction Files: Card No. 84-0307, database edition, The International Center for Diffraction Data (ICDD)
  • [19] Powder Diffraction Files: Card No. 39-1346, database edition, The International Center for Diffraction Data (ICDD)
  • [20] Powder Diffraction Files: Card No. 73-1739, database edition, The International Center for Diffraction Data (ICDD)
  • [21] Powder Diffraction Files: Card No. 07-0233, database edition, The International Center for Diffraction Data (ICDD)
  • [22] Powder Diffraction Files: Card No. 85-0852, database edition, The International Center for Diffraction Data (ICDD)
  • [23] R.M. Cornell, U. Schwertmann, The Iron Oxides, Wiley-VCH, Weinheim 2003, p. 382, doi: 10.1002/3527602097
  • [24] Powder Diffraction Files: Card No. 78-0133, database edition, The International Center for Diffraction Data (ICDD)
  • [25] Z. Jin, W. Tang, J. Zhang, H. Lin, Y. Du, J. Magn. Magn. Mater. 182, 231 (1998), doi: 10.1016/S0304-8853(97)00679-3
  • [26] R. Nowosielski, R. Babilas, G. Dercz, L. Pajak, W. Skowronski, J. Achiev. Mater. Manufact. Eng. 27, 51 (2008)
Document Type
Publication order reference
YADDA identifier
bwmeta1.element.bwnjournal-article-appv128n325kz
Identifiers
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.