A Study on Hardfacing Alloy Using Fe-Cr and Fe-B Powders

Content
Title variants
Languages of publication
EN
Abstracts
EN
The aim of this study is the investigation of the effect of ferroboron and ferrochromium with massive wire based hardfacing alloys. Mixture of Fe-Cr and Fe-B powders was added to massive wire during welding process. Hardface layers were obtained by three different powder mixture and three different powder/massive wire proportions. Hardfacing was applied to two AISI 1020 steel substrates by open arc welding. Hardness test, scanning electron microscope and X-ray diffraction analysis were made to the samples. Test results showed that increasing ferroboron content and increasing powder mixture amount enhanced the microhardness of the specimens.
Keywords
EN
Publisher

Year
Volume
128
Issue
2B
Pages
B-160-B-163
Physical description
Dates
published
2015-8
Contributors
author
  • Firat University, Metallurgy and Materials Engineering, Elazig, Turkey
author
  • Firat University, Metallurgy and Materials Engineering, Elazig, Turkey
author
  • Firat University, Metallurgy and Materials Engineering, Elazig, Turkey
References
  • [1] R. Davis, ASM Handbook, Welding, Brazing and Soldering, Vol. 6, ASM International, USA 1993, p. 787
  • [2] I. Khan, Welding Science and Technology, 1st ed., New Age International (P), New Delhi 2007
  • [3] S.Y. Tu, M.D. Jean, J.T. Wang, C.S. Wu, Int. J. Adv. Manuf. Technol. 27, 889 (2006), doi: 10.1007/s00170-004-2265-6
  • [4] H. Deng, H. Shi, S. Tsuruoka, Surf. Coat. Technol. 204, 3927 (2010), doi: 10.1016/j.surfcoat.2010.05.013
  • [5] M. Shamanian, S.M.R. Mousavi Abarghouie, S.R. Mousavi Pour, Mater. Des. 31, 2760 (2010), doi: 10.1016/j.matdes.2010.01.017
  • [6] M. Kirchgabner, E. Badisch, F. Franek, Wear 265, 772 (2008), doi: 10.1016/j.wear.2008.01.004
  • [7] G. Azimi, M. Shamanian, J. Mater. Sci. 45, 842 (2010), doi: 10.1007/s10853-009-4008-4
  • [8] E. Badich, C. Katsich, H. Winkelmann, F. Franek, M. Roy, Tribol. Int. 43, 1234 (2010), doi: 10.1016/j.triboint.2010.01.008
  • [9] J.J. Coronado, H.F. Caicedo, A.L. Gomez, Tribol. Int. 42, 745 (2009), doi: 10.1016/j.triboint.2008.10.012
  • [10] L. Lin, K. Han, Surf. Coat. Technol. 106, 100 (1998)
  • [11] B. Selcuk, R. İpek, M.B. Karamis, J. Kuzucu, J. Mater. Proc. Technol. 103, 310 (2000)
  • [12] J.W. Yoo, S.H. Lee, C.S. Yoon, S.J. Kim, J. Nucl. Mater. 352, 90 (2006), doi: 10.1016/j.jnucmat.2006.02.071
  • [13] J.H. Kim, H.S. Hong, S.J. Kim, Mater. Lett. 61, 1235 (2007), doi: 10.1016/j.matlet.2006.07.015
  • [14] R.J. Chung, X. Tang, D.Y. Li, B. Hinckley, K. Dolman, Wear 301, 695 (2013), doi: 10.1016/j.wear.2013.01.079
  • [15] M.H. Amushahi, F. Ashrafizadeh, M. Shamanian, Surf. Coat. Technol. 204, 2723 (2012), doi: 10.1016/j.surfcoat.2010.02.028
  • [16] S.T. Petrovic, S.V. Markovic, S. Zec, J. Serb. Chem. Soc. 67, 697 (2002), doi: 10.2298/JSC0210697T
  • [17] M. Eroğlu, Surf. Coat. Technol. 203, 2229 (2009), doi: 10.1016/j.surfcoat.2009.02.010
  • [18] P.K. Liao, K.E. Spear, ASM Handbook, Alloy Phase Diagrams, Vol. 3, ASM International, Materials Park, OH 1992, p. 81
  • [19] H. Okamoto, in Ref. [18], p. 110
  • [20] X.H. Tang, R. Chung, C.J. Pang, D.Y. Li, B. Hinckley, K. Dolman, Wear 271, 1426 (2011), doi: 10.1016/j.wear.2010.11.047
  • [21] C.M. Lin, H.H. Lai, J.C. Kuo, W. Wu, Mater. Charact. 62, 1124 (2011), doi: 10.1016/j.matchar.2011.09.007
Document Type
Publication order reference
YADDA identifier
bwmeta1.element.bwnjournal-article-appv128n2b043kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.