2015 | 128 | 2B | B-118-B-121
Article title

Characteristics of Samaria-Doped Ceria Prepared by Pechini Method

Content
Title variants
Languages of publication
EN
Abstracts
EN
CeO₂ ceramics doped with 20 mol.% samarium (SDC-20) were prepared through the Pechini process. The samples were calcined at 400, 700 and 1000°C. The sintering behavior of the calcined SDC-20 powders was also investigated at 1400°C for 6 h. Microstructural and physical properties of SDC-20 samples were characterized with X-ray diffraction, scanning electron microscopy, thermogravimetry and impedance analysis methods. The results of the thermogravimetry/differential thermal analysis and X-ray diffraction indicated that a single-phase fluorite structure formed at a relatively low calcination temperature of 400°C. It is understood from the measured ionic conductivity values that the pellet formed from the SDC-20 samples calcined at 1000°C had lower resistance of grain-boundary than those of the pellets formed from the SDC-20 samples calcined at 400 and 700°C. The maximum ionic conductivity was measured as 1.95× 10⁻² S cm⁻¹ at 800°C for the sintered SDC-20 pellet obtained from SDC-20 powders calcined at 1000°C.
Keywords
EN
Publisher

Year
Volume
128
Issue
2B
Pages
B-118-B-121
Physical description
Dates
published
2015-8
Contributors
author
  • Istanbul University, Faculty of Engineering, Department of Metallurgical Engineering, Avcilar 34320, Istanbul, Turkey
author
  • Istanbul University, Faculty of Engineering, Department of Metallurgical Engineering, Avcilar 34320, Istanbul, Turkey
References
  • [1] J.P.P. Huijsmans, F.P.F. van Berkel, G.M. Christie, J. Power Sources 71, 107 (1998), doi: 10.1016/S0378-7753(97)02789-4
  • [2] H. Yoshida, K. Miura, T. Fukui, S. Ohara, T. Inagaki, J. Power Sources 106, 136 (2002), doi: 10.1016/S0378-7753(01)01038-2
  • [3] H. Yahiro, Y. Eguchi, K. Eguchi, H. Arai, J. Appl. Electrochem. 18, 527 (1988), doi: 10.1007/BF01022246
  • [4] B.C.H. Steele, in: High Conductivity Solid Ionic Conductors - Recent Trends and Applications, Ed. T. Takahashi, World Sci., London 1989, p. 402. ISBN: 9971-50-750-1
  • [5] M.M.A. Sekar, S.S. Manoharan, K.C. Patil, J. Mater. Sci. Lett. 9, 1205 (1990), doi: 10.1007/BF00721893
  • [6] G.S. Wu, T. Xie, X.Y. Yuan, B.C. Cheng, L.D. Zhang, Mater. Res. Bull. 39, 1023 (2004), doi: 10.1016/j.materresbull.2004.03.006
  • [7] Y.X. Li, W.F. Chen, X.Z. Zhou, Mater. Lett. 59, 48 (2005), doi: 10.1016/j.matlet.2004.05.089
  • [8] Y.C. Zhou, M.N. Rahman, J. Mater. Res. 8, 1680 (1993), doi: 10.1557/JMR.1993.1680
  • [9] T. Matsui, K. Fujiwara, K. Machida, G. Adachi, T. Sakata, H. Mori, Chem. Mater. 9, 2197 (1997), doi: 10.1021/cm970359v
  • [10] C.R. Xia, M.L. Liu, Solid State Ionics 152, 423 (2002), doi: 10.1016/S0167-2738(02)00381-8
  • [11] H.C. Jang, D.S. Jung, J.H. Kim, Y.C. Kang, Y.H. Cho, J.H. Lee, Ceram. Int. 36, 465 (2010), doi: 10.1016/j.ceramint.2009.09.015
  • [12] A. Arabaci, M.F. Öksüzömer, Ceram. Int. 38, 6509 (2012), doi: 10.1016/j.ceramint.2012.05.030
  • [13] T.S. Zhang, J. Ma, Y.Z. Chen, L.H. Luo, L.B. Kong, S.H. Chan, Solid State Ionics 177, 1227 (2006), doi: 10.1016/j.ssi.2006.05.006
  • [14] D.Y. Wang, A.S. Nowick, J. Solid State Chem. 35, 325 (1980), doi: 10.1016/0022-4596(80)90529-0
Document Type
Publication order reference
YADDA identifier
bwmeta1.element.bwnjournal-article-appv128n2b032kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.