Effect of Tungsten Addition on Phase Constitution and Magnetic Properties of the Bulk Fe_{65}Pr_{9}B_{26-x}W_x Alloys

Content
Title variants
Languages of publication
EN
Abstracts
EN
The effect of tungsten addition on phase constitution and magnetic properties of the bulk Fe_{65}Pr_9B_{26-x}W_{x} (where x=2, 4, 6, 8) alloys was studied. The base alloys were prepared by arc-melting of the high purity elements under Ar atmosphere. Samples were produced by suction of an arc-molten alloy to a water-cooled copper mould (the suction-casting method). In order to develop nanocrystalline structure, the samples were subjected to annealing. Heat treatment resulted in an evolution of the phase constitution that caused changes in magnetic properties of the alloys. X-ray diffractometry was used to determine the phase composition of annealed samples. The analysis showed presence of hard magnetic Pr_2Fe_{14}B, paramagnetic Pr_{1+x}Fe_4B_4 and soft ferromagnetic α-Fe phases of annealed samples. The room temperature magnetic properties were determined from hysteresis loops measured by VSM magnetometer in the external magnetic field up to 2 T. The highest hard magnetic parameters were measured for the rod sample of Fe_{65}Pr_9B_{20}W_6 annealed at 1003 K for 5 min.
Keywords
EN
Year
Volume
128
Issue
1
Pages
104-106
Physical description
Dates
published
2015-7
received
2015-02-02
References
  • [1] J.F. Herbst, W.B. Yelon, J. Appl. Phys. 57, 2343 (1985), doi: 10.1063/1.334342
  • [2] E.P. Wohlfarth, K.H.J. Buschow, Ferromagnetic Materials, North-Holland, Amsterdam 1988, p. 20, Table 4
  • [3] S. Hirosawa, Y. Matsuura, H. Yamamoto, S. Fujimura, M. Sagawa, H. Yamauchi, J. Appl. Phys. 59, 873 (1986), doi: 10.1063/1.336611
  • [4] E.B. Boltich, W.E. Wallace, Solid State Commun. 55, 529 (1985), doi: 10.1016/0038-1098(85)90328-X
  • [5] W. Rodewald, P. Scherey, J. Magn. Magn. Mater. 83, 206 (1990), doi: 10.1016/0304-8853(90)90487-B
  • [6] J. Bernardi, J. Fidler, F. Födermayr, IEEE Trans. Magn. 28, 2127 (1992), doi: 10.1109/20.179418
  • [7] A. Yan, X. Song, X. Wang, IEEE Trans. Magn. 36, 2033 (2000), doi: 10.1109/20.875316
  • [8] A. Yan, W. Song, M. Song, W. Wang, J. Alloys Comp. 257, 273 (1997), doi: 10.1016/S0925-8388(97)00003-0
  • [9] J.F. Herbst, J.J. Croat, J. Magn. Magn. Mater. 100, 57 (1991), doi: 10.1016/0304-8853(91)90812-O
  • [10] B. Xiaoqian, Z. Jie, L. Wei, G. Xuexu, Z. Shouzeng, J. Rare Earth 27, 843 (2000), doi: 10.1016/S1002-0721(08)60347-6
  • [11] A. Przybył, J.J. Wysłocki, J. Mater. Process. Technol. 175, 352 (2006), doi: 10.1016/j.jmatprotec.2005.04.064
  • [12] A. Przybył, K. Pawlik, P. Pawlik, P. Gębara, J.J. Wysłocki, J. Alloys Comp. 536, 333 (2012), doi: 10.1016/j.jallcom.2011.11.108
  • [13] K. Pawlik, P. Pawlik, J.J. Wysłocki, W. Kaszuwara, J. Alloys Comp. 536, 348 (2012), doi: 10.1016/j.jallcom.2011.12.003
  • [14] K. Pawlik, J. Bednarcik, P. Pawlik, J.J. Wysłocki, W. Kaszuwara, B. Michalski, P. Gębara, Phys. Status Solidi C 7, 1336 (2010), doi: 10.1002/pssc.200983367
  • [15] P. Pawlik, K. Pawlik, H.A. Davies, J.J. Wysłocki, P. Gębara, Phys. Status Solidi A 207, 1174 (2010), doi: 10.1002/pssa.200983369
  • [16] K. Filipecka, K. Pawlik, P. Pawlik, J.J. Wysłocki, P. Gebara, A. Przybył, Acta Phys. Pol. A 126, 164 (2014), doi: 10.12693/APhysPolA.126.164
  • [17] J.J. Wysłocki, P. Pawlik, J. Achievem. Mater. Manufact. Eng. 43, 463 (2010)
Document Type
Publication order reference
YADDA identifier
bwmeta1.element.bwnjournal-article-appv128n122kz
Identifiers
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.