Sintering Behavior and Machinability Properties of Industrial Waste Materials Based Glass-Ceramics

Content
Title variants
Languages of publication
EN
Abstracts
EN
Glass-ceramics were produced by sintering method from industrial waste materials such as fly ash, blast furnace slag and boron waste. The sintering behavior and machinability of glass-ceramic compositions were investigated. Additives were added to waste materials for enhancement of machinability and sintering properties. All starting materials were mixed by ball milling for 2 h using alumina media. The mixed and milled powders were sieved to grain sizes smaller than 75 μm and pressed at 100 MPa. The pressed samples were sintered at 900°C, 1000°C and 1100°C for 1 h in an electric furnace using a heating rate of 5°C/min. Some characterization tests such as X-ray diffraction (XRD), scanning electron microscopy (SEM) and machinability tests were performed on sintered samples. The results indicated that all samples exhibit good sintering and machinability properties.
Keywords
Contributors
author
  • Sakarya University, Department of Welding Technology, Arifiye Vocational High School, 54580 Arifiye, Sakarya, Turkey
author
  • Sakarya University, Engineering Faculty, Department of Metallurgical and Materials Engineering, Esentepe Campus, 54187 Sakarya, Turkey
author
  • Sakarya University, Engineering Faculty, Department of Metallurgical and Materials Engineering, Esentepe Campus, 54187 Sakarya, Turkey
References
  • [1] A.A. Francis, Mat. Research Bull. 41, 1146 (2006), doi: 10.1016/j.materresbull.2005.11.002
  • [2] S. Yilmaz, G. Bayrak, S. Sen, U. Sen, Mat. & Design. 27, 1092 (2006), doi: 10.1016/j.matdes.2005.04.004
  • [3] S. Yilmaz, O.T. Ozkan, V. Gunay, Ceram. Int. 22, 477 (1996), doi: 10.1016/0272-8842(95)00118-2
  • [4] G. Bayrak, S. Yilmaz, Acta Phys. Pol. A. 125, 623 (2014), doi: 10.12693/APhysPolA.125.623
  • [5] E. Ercenk, S. Yilmaz, Acta Phys. Pol. A. 125, 629 (2014), doi: 10.12693/APhysPolA.125.629
  • [6] D.U. Tulyaganov, M.J. Ribeiro, J.A. Labrincha, Ceram. Int. 28, 515 (2002), doi: 10.1016/S0272-8842(02)00004-4
  • [7] M. Erol, S. Kucukbayrak, A.E. Mericboyu, M.L. Ovecoglu, Jour. Eur. Cer. Soc. 21, 2835 (2001), doi: 10.1016/S0955-2219(01)00221-7
  • [8] R.D. Rawlings, J.P. Wu, A.R. Boccaccini, Jour. Mat. Sci. 41, 733 (2006), doi: 10.1007/s10853-006-6554-3
  • [9] A.M. Nassar, E.M.A. Hamzawy, F.M. Hafez, S.S. El Dera, C. Rüssel, Ceram. Int. 38, 1921 (2012), doi: 10.1016/j.ceramint.2011.10.022
  • [10] D.U. Tulyaganov, S. Agathopoulos, H.R. Fernandes, J.M. Ventura, J.M.F. Ferreira, Jour. Euro. Ceram. Soc. 24, 3521 (2004), doi: 10.1016/j.jeurceramsoc.2003.11.026
  • [11] S. Taruta, T. Ichinose, T. Yamaguchi, K. Kitajima, Jour. Non-Cryst. Solids. 352, 5556 (2006), doi: 10.1016/j.jnoncrysol.2006.09.028
  • [12] J. Wu, Z. Li, Y. Huang, F. Li, Ceram. Int. 39, 7743 (2013), doi: 10.1016/j.ceramint.2013.03.031
  • [13] J. Henry, R.G. Hill, Jour. Non-Cryst. Solids. 319, 13 (2003), doi: 10.1016/S0022-3093(02)01959-2
  • [14] T. Höche, S. Habelit z, I.I. Khodos, J. Cryst. Growth. 192, 185 (1998), doi: 10.1016/S0022-0248(98)00458-8
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv127n4133kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.