Phase Transitions in Fe-Rh Alloys Induced by Temperature

• Authors: V. Rodionov , V. Rodionova , M. Annaorazov
• Languages of publication: EN

Abstracts

EN

This research work was aimed to find the composition of equiatomic Fe-Rh alloy and to find the way of preparation of samples with extremely narrow thermal hysteresis and repeatable results. Alloys with content of Fe from 48 up to 52 at.% were examined. Fe-Rh alloys were prepared in forms of bulk piece, plate and wire. The plates of alloys were found to be more perspective for further investigations. The influence of parameters of ingot and samples treatments on antiferromagnetic-ferromagnetic transition was studied. The ways of narrowing of temperature hysteresis were established.

Keywords

EN

64.60.Cn; 75.30.Kz; 64.70.K-

Discipline

• 64.70.K-: Solid-solid transitions(see also 61.50.Ks Crystallographic aspects of phase transformations; pressure effects; 75.30.Kz and 77.80.B- for magnetic and ferroelectric transitions, respectively; for materials science aspects, see 81.30.-t)
• 75.30.Kz: Magnetic phase boundaries (including classical and quantum magnetic transitions, metamagnetism, etc.)(for ferroelectric phase transitions, see 77.80.B-; for superconductivity phase diagrams, see 74.25.Dw)
• 64.60.Cn: Order-disorder transformations(see also 81.30.Hd Constant-composition solid-solid phase transformations: polymorphic, massive, and order-disorder in materials science; for effects of disorder on superconducting transition temperature, see 74.62.En)

• Publisher: Institute of Physics, Polish Academy of Sciences
• Journal: Acta Physica Polonica A
• Year: 2015
• Volume: 127
• Issue: 2
• Pages: 445-447

Dates

published

2015-02

Contributors

author

V. Rodionov

• Innovation Park and Institute of Physics and Technology, Immanuel Kant Baltic Federal University, Nevsky 14, Kaliningrad 236041, Russia

author

V. Rodionova

• Innovation Park and Institute of Physics and Technology, Immanuel Kant Baltic Federal University, Nevsky 14, Kaliningrad 236041, Russia
• National University of Science and Technology MISiS, Leninsky 4, 119049, Moscow, Russia

author

M. Annaorazov

• Innovation Park and Institute of Physics and Technology, Immanuel Kant Baltic Federal University, Nevsky 14, Kaliningrad 236041, Russia

References

• [1] M.P. Annaorazov, M. Unal, S.A. Nikitin, A.L. Tyurin, K.A. Asatryan, J. Magn. Magn. Mater. 251, 61 (2002), doi: 10.1016/S0304-8853(02)00477-8
• [2] M.P. Annaorazov, H.M. Guven, K. Barner, J. Alloys Comp. 397, 26 (2005), doi: 10.1016/j.jallcom.2005.01.016
• [3] R. Sindhunil Barman, J. Phys. Condens. Matter 25, 183201 (2013), doi: 10.1088/0953-8984/25/18/183201
• [4] D.W. Cooke, F. Hellman, C. Baldasseroni, C. Bordel, S. Moyerman, E.E. Fullerton, Phys. Rev. Lett. 109, 255901 (2012), doi: 10.1103/PhysRevLett.109.255901
• [5] X. Marti, I. Fina, C. Frontera, J. Liu, P. Wadley, Q. He, R.J. Paull, J.D. Clarkson, J. Kudrnovský, I. Turek, J. Kuneš, D. Yi, J.-H. Chu, C.T. Nelson, L. You, E. Arenholz, S. Salahuddin, J. Fontcuberta, T. Jungwirth, R. Ramesh, Nature Mater. 13, 367 (2014), doi: 10.1038/NMAT3861
• [6] L. Pal, T. Tarnoczi, P. Szabo, E. Kren, J. Toth, in: Proc. Int. Conf. on Magnetism, Nottingham 1964, p. 158

Identifiers

DOI

10.12693/APhysPolA.127.445