2014 | 126 | 4 | 979-983
Article title

Mechanical Alloying of Al_{73}Cu_{11}Cr_{16} Alloy from Ion Irradiated Powders

Content
Title variants
Languages of publication
EN
Abstracts
EN
Al_{73}Cu_{11}Cr_{16} alloys were prepared by mechanical alloying of the irradiated by Ar^{+} ions elemental powders. Evolution of alloy structure at ball milling, as well as during the further annealing, was investigated using X-ray diffraction and differential scanning calorimetry. It was shown that ball milling leads to the Cu dissolution in Al and Cr and to the formation of Al_{2}Cu intermetallic phase. An increase of the milling duration leads to an increase of the Al_{2}Cu phase content in the samples. Ion irradiation of initial elemental powders results in an increase of their interaction rate at milling. In the case of irradiated powders using as initial materials, a content of Al_{2}Cu phase after milling is higher than in the case of using non-irradiated elemental powders. No effect of irradiation of initial elemental powders on the phase transformation at heating was observed. The annealing results in the decomposition of Al- and Cr-based supersaturated solid solutions. An increase in the Al_{2}Cu phase content at heating was observed only in the samples, which were milled for 4 h. In the samples milled for 14 h, nearly no increase in Al_{2}Cu phase content at heating was observed. Heating up to 500-600°C results in the single-phase decagonal quasicrystalline phase formation for all of the studied samples.
Keywords
EN
Year
Volume
126
Issue
4
Pages
979-983
Physical description
Dates
published
2014-10
References
  • [1] D.J. Sordelet, J.M. Dubois, MRS Bull. 22, 34 (1997), doi: 10.1557/S0883769400034400
  • [2] J.E. Shield, M.J. Kramer, R.W. McCallum, J. Mater. Res. 8, 1199 (1993), doi: 10.1557/JMR.1993.1199
  • [3] A. Inoue, H. Kimura, Nanostruct. Mater. 11, 221 (1999), doi: 10.1016/S0965-9773(99)00035-5
  • [4] N.S. Cohen, O.A. Pankhurst, L.F. Barquin, J. Phys. Condens. Matter. 11, 8839 (1999), doi: 10.1088/0953-8984/11/45/308
  • [5] V.V. Tcherdyntsev, S.D. Kaloshkin, I.A. Tomilin, E.V. Shelekhov, Yu.V. Baldokhin, Nanostruct. Mater. 12, 139 (1999), doi: 10.1016/S0965-9773(99)00083-5
  • [6] E.Yu. Ivanov, I.G. Konstanchuk, B.D. Bokhonov, V.V. Boldyrev, React. Solids 7, 167 (1989), doi: 10.1016/0168-7336(89)80026-9
  • [7] J. Eckert, L. Schultz, K. Urban, Mater. Sci. Eng. A 133, 393 (1991), doi: 10.1016/0921-5093(91)90095-5
  • [8] J. Eckert, L. Schultz, K. Urban, Acta Metall. Mater. 39, 1497 (1991), doi: 10.1016/0956-7151(91)90235-S
  • [9] N. Asahi, Mater. Sci. Eng. A 226-228, 69 (1997), doi: 10.1016/S0921-5093(97)80025-1
  • [10] F. Schurak, J. Eckert, L. Schultz, Nanostruct. Mater. 12, 107 (1999), doi: 10.1016/S0965-9773(99)00075-6
  • [11] V. Srivinas, P. Barua, B.S. Murty, Mater. Sci. Eng. A 294-296, 65 (2000), doi: 10.1016/S0921-5093(00)01200-4
  • [12] A.I. Salimon, A.M. Korsunsky, E.V. Shelekhov, T.A. Sviridova, Mater. Sci. Forum 294-296, 676 (2000), doi: 10.4028/www.scientific.net/MSF.321-324.676
  • [13] A.I. Salimon, A.M. Korsunsky, S.D. Kaloshkin, V.V. Tcherdyntsev, E.V. Shelekhov, T.A. Sviridova, Mater. Sci. Forum 321-324, 137 (2000), doi: 10.4028/www.scientific.net/JMNM.10.137
  • [14] A.M. Korsunsky, E.V. Shelekhov, T.A. Sviridova, S.D. Kaloshkin, V.V. Tcherdyntsev, Yu.V. Baldokhin, Acta Mater. 49, 1821 (2001), doi: 10.1016/S1359-6454(01)00077-5
  • [15] S.D. Kaloshkin, V.V. Tcherdyntsev, A.I. Salimon, I.A. Tomilin, T. Spataru, G. Principi, Hyperfine Interact. 139/140, 399 (2002), doi: 10.1023/A:1021241905130
  • [16] V.V. Tcherdyntsev, S.D. Kaloshkin, A.I. Salimon, I.A. Tomilin, A.M. Korsunsky, J. Non-Cryst. Solids 312-314, 399 (2002), doi: 10.1016/S0022-3093(02)01745-3
  • [17] P.D. Bloom, K.G. Baikerikar, J.U. Otaigbe, V.V. Sheares, Mater. Sci. Eng. A 294-296, 156 (1997), doi: 10.1016/S0921-5093(00)01230-2
  • [18] B.C. Anderson, P.D. Bloom, K.G. Baikerikar, V.V. Sheares, S.K. Mallapragada, Biomaterials 23, 1761 (2002), doi: 10.1016/S0142-9612(01)00301-5
  • [19] S.D. Kaloshkin, V.V. Tcherdyntsev, V.D. Danilov, Cryst. Rep. 52, 953 (2007), doi: 10.1134/S1063774507060053
  • [20] F. Ali, S. Scudino, M.S. Anwar, R.N. Shahid, V.C. Srivastava, V. Uhlenwinkel, M. Stoica, G. Vaughan, J. Eckert, J. Alloys Comp. 607 274, (2014), doi: 10.1016/j.jallcom.2014.04.086
  • [21] S.D. Kim, D.S. Ko, W.K. Jang, K.S. Shin, Y.W. Kim, Mater. Sci. Eng. A 528, 4845 (2011), doi: 10.1016/j.msea.2011.02.044
  • [22] S.D. Kaloshkin, V.V. Tcherdyntsev, A.I. Laptev, A.A. Stepashkin, E.A. Afonina, A.L. Pomadchik, V.I. Bugakov, J. Mater. Sci. 39, 5399 (2004), doi: 10.1023/B:JMSC.0000039253.28721.3f
  • [23] E. Huttunen-Saarivirta, J. Alloys Comp. 363, 150 (2004), doi: 10.1016/S0925-8388(03)00445-6
  • [24] A. Rüdiger, U. Köster, Mater. Sci. Eng. A 294-296, 890 (2000), doi: 10.1016/S0921-5093(00)01037-6
  • [25] V.V. Cherdyntsev, E.A. Leonova, S.D. Kaloshkin, Phys. Met. Metallogr. 95, 478 (2003)
  • [26] V.V. Tcherdyntsev, T.A. Sviridova, A.P. Shevchukov, S.D. Kaloshkin, Z. Kristallogr. 223, 751 (2008), doi: 10.1524/zkri.2008.1079
  • [27] T.A. Sviridova, A.P. Shevchukov, E.V. Shelekhov, D.L. Diakonov, V.V. Tcherdyntsev, S.D. Kaloshkin, J. Alloys Comp. 509, S299 (2011), doi: 10.1016/j.jallcom.2010.12.074
  • [28] A.P. Shevchukov, T.A. Sviridova, S.D. Kaloshkin, V.V. Tcherdyntsev, M.V. Gorshenkov, M.N. Churyukanova, D. Zhang, Z. Li, J. Alloys Comp. 586, S391 (2014), doi: 10.1016/j.jallcom.2013.02.043
  • [29] N.V. Gavrilov, S.P. Nikulin, G.V. Radkovskii, Instrum. Exp. Tech. 39, 81 (1996)
  • [30] E.V. Shelekhov, T.A. Sviridova, Met. Sci. Heat Treatm. 42, 309 (2000)
  • [31] Binary Alloys Phase Diagrams, Ed. T.B. Massalski, Am. Soc. Met., 1987
  • [32] R.Z. Chen, C.J. Lin, D.X. Li, J.X. Zheng, Acta Phys. Sin. 30, 555 (1981)
  • [33] N. Ponweiser, C.L. Lengauer, K.W. Richter, Intermetallics 19, 1737 (2011), doi: 10.1016/j.intermet.2011.07.007
  • [34] C. Suryanarayana, Prog. Mater. Sci. 46, 1 (2001), doi: 10.1016/S0079-6425(99)00010-9
  • [35] V.V. Cherdyntsev, S.D. Kaloshkin, V.N. Serdyukov, I.A. Tomilin, E.V. Shelekhov, Phys. Met. Metallogr. 97, 392 (2004)
  • [36] I. Lichioiu, I. Peter, B. Varga, M. Rosso, J. Mater. Sci. Tech. 30, 294 (2014), doi: 10.1016/j.jmst.2013.12.001
  • [37] L.I. Mirkin, Handbook of X-ray Analysis of Polycrystalline Materials, Consultants Bureau, New York 1964
Document Type
Publication order reference
YADDA identifier
bwmeta1.element.bwnjournal-article-appv126n427kz
Identifiers
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.