Phase Composition and Magnetic Properties of the Nanocrystalline Fe_{64.32}Pr_{9.6}B_{22.08}W_{4} Alloy

Content
Title variants
Languages of publication
EN
Abstracts
EN
The aim of the present work was to study the influence of annealing conditions on magnetic properties and the phase constitution of rapidly solidified Fe_{64.32}Pr_{9.6}B_{22.08}W_{4} alloy ribbons. The base alloy was prepared by arc-melting of the high purity elements under an Ar atmosphere. Subsequently the ribbon samples were obtained by melt-spinning technique under low pressure of Ar. In order to develop nanocrystalline structure, the samples were annealed at 1003 K for 5, 10, 20 and 30 min. The room temperature magnetic properties were determined from hysteresis loops measured by VSM magnetometry in the external magnetic field up to 2 T. For comparison the influence of annealing temperature on magnetic properties was studied for the same alloy composition. The ribbons were annealed at temperatures from 929 K to 1023 K for 5 min. X-ray diffractometry was used to determine the phase composition of annealed ribbons. Heat treatment resulted in an evolution of the phase constitution, that caused changes in magnetic properties of the alloy.
Keywords
EN
Year
Volume
126
Issue
1
Pages
164-165
Physical description
Dates
published
2014-07
References
  • [1] M. Sagawa, S. Fujimura, N. Togawa, H. Yamamoto, Y. Matsuura, J. Appl. Phys. 55, 2083 (1984), doi: 10.1063/1.333572
  • [2] J.J. Corat, J.F. Herbst, R.W. Lee, F.E. Pinkerton, J. Appl. Phys. 55, 2078 (1984), doi: 10.1063/1.333571
  • [3] A. Przybył, I. Wnuk, P. Gębara, J.J. Wysłocki, JAMME 49/2, 210 (2011). http://www.journalamme.org/papers_vol49_2/49211.pdf
  • [4] A. Przybył, K. Pawlik, P. Pawlik, P. Gębara, J.J. Wysłocki, J. Alloys Compd. 536, S333 (2012), doi: 10.1016/j.jallcom.2011.11.108
  • [5] K. Pawlik, P. Pawlik, J.J. Wysłocki, HUKHUKActa Phys. Pol. A 118, 900 (2010)
  • [6] K. Pawlik, P. Pawlik, J.J. Wysłocki, W. Kaszuwara, J. Alloys Compd. 536, S348 (2012), doi: 10.1016/j.jallcom.2011.12.003
  • [7] K. Pawlik, J. Bednarcik, P. Pawlik, J.J. Wysłocki, W. Kaszuwara, B. Michalski, P. Gębara, Phys. Stat. Sol. C 7, 1336 (2010), doi: 10.1002/pssc.200983367
  • [8] P. Pawlik, K. Pawlik, H.A. Davies, J.J. Wysłocki, P. Gębara, Phys. Stat. Sol. A 207, 1174 (2010), doi: 10.1002/pssa.200983369
Document Type
Publication order reference
YADDA identifier
bwmeta1.element.bwnjournal-article-appv126n1078kz
Identifiers
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.