Effect of Annealing Time on Structure of Fe_{72.5}Cu_{1}Nb_{2}Mo_{2}Si_{15.5}B_{7} Alloy

Content
Title variants
Languages of publication
EN
Abstracts
EN
The process of a primary crystallization of the Fe_{72.5}Cu_{1}Nb_{2}Mo_{2}Si_{15.5}B_{7} alloys was investigated by differential thermal analysis (DTA), x-ray diffraction (XRD) and transmission electron microscopy (TEM). Amorphous ribbons were isothermally annealed for 0.5, 2, 6, 30 and 150 minutes at 520 °C. Both, the XRD and TEM study showed that the level of devitrification of the sample increases with the annealing time. The above mentioned techniques confirmed the presence of the nanocrystalline grains of the Fe_{3}Si phase and enable us to study the evolution of the identified phase.
Keywords
EN
Contributors
author
  • Institute of Physics, Faculty of Science, P.J. Šafárik University, Park Angelinum 9, 041 54 Košice, Slovakia
author
  • Institute of Physics, Faculty of Science, P.J. Šafárik University, Park Angelinum 9, 041 54 Košice, Slovakia
  • Institute of Physics, Faculty of Science, P.J. Šafárik University, Park Angelinum 9, 041 54 Košice, Slovakia
author
  • ELI-Beamlines, Institute of Physics of the ASCR, v. v. i., Na Slovance 2, 182 21 Praha 8, Czech Republic
  • HASYLAB am DESY, Notkestrasse 85, D-22503 Hamburg, Germany
author
  • Institute of Chemistry, Faculty of Science, P.J. Šafárik University, Moyzesova 11, 041 54 Košice, Slovakia
author
  • Institute of Physics, Faculty of Science, P.J. Šafárik University, Park Angelinum 9, 041 54 Košice, Slovakia
References
  • [1] M.E. McHenry, M.A. Willard, D.E. Laughlin, Prog. Mater. Sci. 44, 291 (1999), doi: 10.1016/S0079-6425(99)00002-X
  • [2] H. Chiriac, T.A. Ovari, Prog. Mater. Sci. 40, 333 (1996), doi: 10.1016/S0079-6425(97)00001-7
  • [3] O. Crisan, J.M. Greneche, J.M. Le Breton, A.D. Crisan, Y. Labaye, L. Berger, G. Filoti, Eur. Phys. J. B 34, 155 (2003), doi: 10.1140/epjb/e2003-00207-3
  • [4] N. Kotaoka, A. Inoue, T. Masumoto, Y. Yoshizawa, K. Yamauchi, Japan. J. Appl. Phys. 28, L1820 (1989), doi: 10.1143/JJAP.28.L1820
  • [5] Y. Yoshizawa, K. Yamauchi, Mat. Res. Soc Symp. Proc. 183 (1991)
  • [6] P. Gorria, V.M. Prida, M. Tejedor, B. Hanando, M.L. Sanchez, Physica B 299, 215 (2001), doi: 10.1016/S0921-4526(01)00468-9
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv126n1054kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.