Sintering Behavior and Machinability in Mica Glass-Ceramic of the System SiO_2-Al_2O_3-MgO-K_2O-B_2O_3-F

Authors
Content
Title variants
Languages of publication
EN
Abstracts
EN
Mica glass-ceramic was prepared by sintering method from in the SiO_2-Al_2O_3-MgO-K_2O-B_2O_3-F_2 system. The sintering behavior and machinability of a glass-ceramic composition were examined. The starting materials were mixed and milled in an alumina ball mill for 2 h. Then the powders were sieved to obtain grain sizes smaller than 75 μm. For the shaping process, disc samples were prepared by pressing at 100 MPa. The pressed discs were sintered at temperatures in the range from 900 to 1200C for 2 h in an electric furnace using a heating rate of 5°C/min. X-ray diffraction analysis, scanning electron microscopy, and machinability tests for characterization were performed on sintered samples. The results showed that all samples exhibited similar phases formation and good machinability.
Keywords
Contributors
author
  • Sakarya University, Engineering Faculty, Department of Metallurgical and Materials Engineering Esentepe Campus, 54187 Sakarya, Turkey
author
  • Sakarya University, Engineering Faculty, Department of Metallurgical and Materials Engineering Esentepe Campus, 54187 Sakarya, Turkey
References
  • 1. D.U. Tulyaganov, M.J. Ribeiro, J.A. Labrincha, doi: 10.1016/S0272-8842(02)00004-4, Ceram. Int. 28, 515 (2002)
  • 2. A.M. Nassar, E.M.A. Hamzawy, F.M. Hafez, S.S. El Dera, C. Rüssel, doi: 10.1016/j.ceramint.2011.10.022, Ceram. Int. 38, 1921 (2012)
  • 3. D.U. Tulyaganov, S. Agathopoulos, H.R. Fernandes, J.M. Ventura, J.M.F. Ferreira, doi: 10.1016/j.jeurceramsoc.2003.11.026, J. Europ. Ceram. Soc. 24, 3521 (2004)
  • 4. S. Taruta, T. Ichinose, T. Yamaguchi, K. Kitajima, doi: 10.1016/j.jnoncrysol.2006.09.028, J. Non-Cryst. Solids 352, 5556 (2006)
  • 5. J. Henry, R.G. Hill, doi: 10.1016/S0022-3093(02)01959-2, J. Non-Cryst. Solids 319, 13 (2003)
  • 6. J. Wu, Z. Li, Y. Huang, F. Li, doi: 10.1016/j.ceramint.2013.03.031, Ceram. Int. 39, 7743 (2013)
  • 7. S. Lakshmi Reddy, N.C. Gangi Reddy, G. Siva Reddy, B. Jagannatha Reddy, R.L. Frost, doi: 10.1016/j.saa.2005.12.030, Spectrochim. Acta A 65, 684 (2006)
  • 8. T. Höche, S. Habelitz, I.I. Khodos, doi: 10.1016/S0022-0248(98)00458-8, J. Cryst. Growth 192, 185 (1998)
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv125n2149kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.