Tribological Behaviors of SiO_2 Added Polyester Matrix Thermosetting Composites

Content
Title variants
Languages of publication
EN
Abstracts
EN
In this study, the tribological behavior of polyester matrix composites filled with silicon dioxide (SiO_2) particles is investigated. The tribological characteristics of pure polyester and 10, 20, 30 and 40 wt% SiO_2 filled polyester composites were comparatively evaluated under dry sliding conditions. Wear tests were carried out at room temperature under the loads of 10, 20, and 30 N at the sliding speed of 1 m/s. The wear test results showed that the SiO_2 particles could improve the wear resistance. The friction coefficient of the polyester was getting increased from 0.228 to 1.1052 with an increase in SiO_2 content depending on applied loads. The results showed that the wear rates of pure polyester and SiO_2 filled polyester composites increased with increase in loads. The wear rates of the SiO_2 filled polyester composites were significantly affected from the SiO_2 content. The wear rate of the polyester changed from 8.0 × 10^{-7} mm^3/m to 1.72 × 10^{-5} mm^3/m depending on SiO_2 contents and applied loads.
Keywords
EN
Year
Volume
125
Issue
2
Pages
560-562
Physical description
Dates
published
2014-02
References
  • 1. B. Wetzel, F. Haupert, M.Q. Zhang, doi: 10.1016/S0266-3538(03)00115-5, Compos. Sci. Technol. 63, 2055 (2003)
  • 2. A. Patnaik, A. Satapathy, S.S. Mahapatra, R.R. Dash, doi: 10.1016/j.matdes.2008.04.057, Mater. Des. 30, 57 (2009)
  • 3. M.T. Albdiry, B.F. Yousif, doi: 10.1016/j.matdes.2012.08.035, Mater. Des. 48, 68 (2013)
  • 4. K.A. Sierros, S.N. Kukureka, doi: 10.1016/j.wear.2007.01.073, Wear 263, 992 (2007)
  • 5. M. Zouari, M. Kharrat, M. Dammak, doi: 10.1016/j.surfcoat.2010.02.001, Surf. Coat. Technol. 204, 2593 (2010)
  • 6. P. Jawahar, R. Gnanamoorthy, M. Balasubramanian, doi: 10.1016/j.wear.2006.01.010, Wear 261, 835 (2006)
  • 7. B. Lepoittevin, N. Pantoustier, M. Devalckenaere, M. Alexandre, C. Calberg, R. Jerome, C. Henrist, A. Rulmont, P. Dubois, doi: 10.1016/S0032-3861(03)00076-4, Polymer 44, 2033 (2003)
  • 8. S. Bahadur, L. Zhang, J.W. Anderegg, doi: 10.1016/S0043-1648(96)07445-5, Wear 203-204, 464 (1997)
  • 9. L.K. El-Gabry, O.G. Allam, O.A. Hakeim, doi: 10.1016/j.carbpol.2012.08.108, Carbohyd. Polym. 92, 353 (2013)
  • 10. G. Xian, R. Walter, F. Haupert, doi: 10.1016/j.compscitech.2005.02.022, Compos. Sci. Technol. 66, 3199 (2006)
  • 11. K. Friedrich, Z. Zhang, A.K. Schlarb, doi: 10.1016/j.compscitech.2005.05.028, Compos. Sci. Technol. 65, 2329 (2005)
  • 12. M.Q. Zhang, M.Z. Rong, S.L. Yu, B. Wetzel, K. Friedrich, doi: 10.1002/1439-2054(20020201)287:2, Macromol. Mater. Eng. 287, 111 (2002)
  • 13. O. Asi, doi: 10.1177/0731684408093975, J. Reinf. Plast. Comp. 28, 2861 (2009)
  • 14. N.K. Myshkin, M.I. Petrokovets, A.V. Kovalev, doi: 10.1016/j.triboint.2005.07.016, Tribol. Int. 38, 910 (2005)
  • 15. M.C. Romanes, N.A. D'Souza, D. Coutinho, K.J. Balkus, T.W. Scharf, doi: 10.1016/j.wear. 2007.08.022, Wear 265, 88 (2008)
Document Type
Publication order reference
YADDA identifier
bwmeta1.element.bwnjournal-article-appv125n2127kz
Identifiers
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.