Article title

Surface Morphological Properties of Mo-Based Thin Films on Glass

Title variants
Languages of publication
In that report we observe the initial stages in the process of film growth at different irradiation doses. Investigations of influence of Mo deposition on glass substrates by means of self-ion-assisted deposition on its topography (atomic force microscopy) and wettability (sessile-drop method) were carried out. It was found out that with an increase of the irradiation dose, the average roughness and the contact angle increases rapidly at first and then decrease. 2.45-2.77 increase in the contact angle of water when Mo-based coating was deposited on the glass was observed.
  • Belarusian State Pedagogical University, Sovetskaya 18, 220050 Minsk, Belarus
  • Belarusian State Pedagogical University, Sovetskaya 18, 220050 Minsk, Belarus
  • Lublin University of Technology, Nadbystrzycka 38d, 20-618 Lublin, Poland
  • 1. K. Orgassa, H.W. Schock, J.H. Werner, Thin Solid Films 431-432, 387 (2003)
  • 2. V.V. Uglov, V.M. Anishchik, V.M. Astashynski, N.N. Cherenda, G.I. Gimro, A.V. Kovyazo, Surf. Coat. Technol. 200, 245 (2005)
  • 3. I.S. Tashlykov, O.G. Bobrovich, V.Ch. Palchekh, V.V. Tuljev, N.V. Alov, V.S. Kulikauskas, G.K. Wolf, Surf. Coat. Technol. 74-75, 945 (1995)
  • 4. I.S. Tashlykov, A.V. Kasperovich, G.K. Wolf, Surf. Coat. Technol. 158-159, 498 (2002)
  • 5. A.L. Suvorov, Yu.N. Cheblukov, N.E. Lazarev, A.F. Bobkov, M.O. Popov, V.P. Babaev, Techn. Phys. 45, 343 (2000)
  • 6. I.S. Tashlykov, A.I. Turavets, P. Zukowski, Acta Phys. Pol. A 120, 115 (2011)
  • 7. Z. Li, D. Chen, X. Fu, W. Miao, Z. Zhang, Adv. Mater. Sci. Eng. 2012, 640462 (2012)
  • 8. A.V. Merkulov, O.A. Merkulova, Techn. Phys. 44, 230 (1999)
  • 9. I. Petrov, P.B. Barna, L. Hultman, J. Greene, J. Vac. Sci. Technol. A 21, S117 (2003)
Document Type
Publication order reference
YADDA identifier
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.