A Comparative Study on the Corrosion Behaviour of Gas Nitrided and TiAlN Coated AISI D2 Steel by Thermo-Reactive Diffusion Technique

Authors
Content
Title variants
Languages of publication
EN
Abstracts
EN
In this study, the corrosion behaviors of nitride and titanium aluminum nitride (TiAlN) layers deposited on AISI D2 steel samples are reported. Steel was at first nitrided in a nitrogen and ammonia atmosphere at 575C for 8 h and then titanium nitride coating treatment was performed in the powder mixture consisting of ferro-titanium, aluminum, ammonium chloride and alumina at 1000C for 2 h by thermo-reactive diffusion technique. Phase analysis and corrosion tests were realized on the titanium aluminum nitride coated steel. The corrosion properties of uncoated and coated samples were characterized by potentiostatic polarization test. The tests were conducted using a three-electrode system test unit with a platinum counter electrode of 2.269 cm^2 and an Ag/AgCl, 3 M KCl electrode as the reference electrode. Nitrided and TiAlN coated steel specimens exhibited higher corrosion resistance than uncoated steel in 0.5 M H_2SO_4 solution. Conclusively, the application of nitride and TiAlN films on AISI D2 steel increased surface hardness and corrosion resistance. TiAlN coating exhibits the highest corrosion resistance.
Keywords
EN
Contributors
author
  • Department of Metal Education, Institute of Arts and Sciences, Sakarya University, 54187 Sakarya, Turkey
author
  • Department of Metallurgical and Materials Engineering, Engineering Faculty, Sakarya University, 54187 Sakarya, Turkey
author
  • Department of Metallurgical and Materials Engineering, Engineering Faculty, Sakarya University, 54187 Sakarya, Turkey
References
  • [1] D. Pye, ASM International, 31 (2003)
  • [2] R. Riedel, Handbook of ceramic hard materials, Wiley-VCH, UK 2000, p. 23
  • [3] Y. Li, L. Qu, F. Wang, Corrosion Sci. 45, 1367 (2003)
  • [4] M. Savaşkan, Y. Taptik, M. Ürgen, Itü J./d Eng. 3, 117 (2004) (in Turkish)
  • [5] G.B. Gaitan, J.C. Caicedo, A.G. Balogh, S. Gottschalk, Phys. Status Solidi C 4, 4260 (2007)
  • [6] A. Schuler, V. Thommen, P. Reimann, P. Oelhafen, J. Vac. Sci. Technol. A 19, 922 (2001)
  • [7] J.F. Marco, J.R. Gancedo, M.A. Auger, O. Sanchez, J.M. Albella, Surf. Interface Anal. 37, 1082 (2005)
  • [8] A. Kovalev, D.L. Wainstein, G. Fox-Rabinovich, K. Yamamoto, S. Veldhius, Surf. Interface Anal. 38, 879 (2006)
  • [9] S. Seal, JOM 59, 51 (2001)
  • [10] A. Kimura, H. Hasegawa, K. Yamada, T. Suzuki, Surf. Coat. Technol. 120-121, 438 (1999)
  • [11] V. Chawla, A. Chawla, Y. Mehta, D. Puri, S.B. Sidhu, J. Austral. Ceram. Soc. 47, 48 (2011)
  • [12] J.L. Huang, B.Y. Shew, J. Am. Ceram. Soc. 82, 696 (1999)
  • [13] R. Baboian, Corrosion Test and Standards, ASTM, Baltimore 2005, p. 109
  • [14] H.C. Barshilia, N. Selvakumar, B. Deepthi, K.S. Rajam, Surf. Coat. Technol. 201, 2193 (2006)
  • [15] H.C. Barshilia, B. Deepthi, K.S. Rajam, K.W. Bhatti, S. Chaudhary, J. Vac. Sci. Technol. A 27, 1 (2009)
  • [16] L. Bai, X. Zhu, J. Xiao, J. He, Surf. Coat. Technol. 201, 5257 (2007)
  • [17] C.H. Lin, J.G. Duh, Surf. Coat. Technol. 204, 784 (2009)
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv123n2035kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.