Investigation of Grain Boundary Compositions and Magnetic Properties of Hot-Worked Nd_{18}Tb_1Fe_{66.5}Co_5Al_{1.5}B_8 Magnets

Content
Title variants
Languages of publication
EN
Abstracts
EN
Magnetic properties which are related to the compositions on the grain boundaries of the NdFeB permanent magnets were studied at different hot working temperatures applied to the cast Nd_{18}Tb_1Fe_{66.5}Co_5Al_{1.5}B_8 ingots. Since the addition of Al caused the formation of hard magnetic μ phase between the magnetic NdFeB crystals after the pressing 800C H_{c} value increased to the highest value of 8.21 kOe. According to the SEM micrographs and EDS analysis, the increase in pressing temperature, the atomic ratios in the NdFeAl compositions approached to hard magnetic μ phase with the increase in pressing temperature and its exact composition was obtained in the sample hot deformed at 800°C. Although the secondary μ phase with a high melting temperature is detremental to the alignment of c axis of the magnetic NdFeB grains along the pressing direction, we found that the magnetic properties of the magnets improve due to the presence of this hard magnetic phase on the grain boundaries.
Keywords
EN
Publisher

Year
Volume
123
Issue
2
Pages
233-234
Physical description
Dates
published
2013-02
Contributors
  • Istanbul Technical University, Metallurgical and Materials Engineering, 34469, Maslak, Istanbul, Turkey
  • Istanbul Technical University, Physics Engineering, 34469 Maslak, Istanbul, Turkey
  • Istanbul Technical University, Metallurgical and Materials Engineering, 34469, Maslak, Istanbul, Turkey
References
  • [1] J.P. Nozieres, R. Perrier de la Bathie, J. Magn. Magn. Mater. 80, 88 (1989)
  • [2] V. Sinka, T. Kvackaj, O.B.G. Assis, M. Ferrante, J. Alloys Comp. 230, 42 (1995)
  • [3] T. Shimoda, K. Akioka, O. Kobayashi, T. Yamagami, T. Ohki, M. Miyagawa, T. Yuri, IEEE Trans. Magn. 25, 4099 (1989)
  • [4] K. Akioka, T. Yamagami, T. Shimoda, J. Appl. Phys. 69, 5829 (1991)
  • [5] J.P. Nozieres, R. Perrier de la Bathie, IEEE Trans. Magn. 25, 4117 (1989)
  • [6] B. Grieb, E.-Th. Henig, G. Martinek, H.H. Stadelmaier, G. Petzow, IEEE Trans. Magn. 26, 1367 (1990)
  • [7] L. Legras, J. Delamera, D. Lemarchand, J. Vu Dinh, P. Vigier, J. Alloys Comp. 218, 17 (1995)
  • [8] B. Grieb, E.-T. Henig Z. Metallkde. 82, 560 (1991)
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv123n2024kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.