Annealing Effects after Various Thermo-Mechanical Treatments on Microstructure and Mechanical Properties of Wrought Magnesium Alloy ZK60

Content
Title variants
Languages of publication
EN
Abstracts
EN
The magnesium alloy ZK60 received from Dead Sea Magnesium in direct-chill cast condition was extruded at T = 350C using an extrusion ratio of ER = 12. The extruded bars were severely plastically deformed at 250C by either equal channel angular pressing or swaging. While swaging led to similar grain refinements as observed after equal channel angular pressing, yield stress and tensile strength values were by far superior in the swaged material. This result is explained by the unfavourable 45° texture component of the (0002) pole figure that develops during the massive shear deformation in equal channel angular pressing. Unlike equal channel angular pressing, the grain orientation after swaging is similar as in the as-extruded condition. Annealing at elevated temperatures indicates very low thermal stability of microstructure and mechanical properties in the equal channel angular pressing material while both properties in the swaged microstructure are as stable as in the as-extruded reference.
Keywords
EN
Publisher

Year
Volume
122
Issue
3
Pages
606-609
Physical description
Dates
published
2012-09
Contributors
author
  • Institute of Materials Science and Technology, Clausthal University of Technology, Clausthal-Zellerfeld, Germany
author
  • Department of Physics of Materials, Charles University, Prague, Czech Republic
author
  • Department of Physics of Materials, Charles University, Prague, Czech Republic
author
  • Institute of Materials Science and Technology, Clausthal University of Technology, Clausthal-Zellerfeld, Germany
References
  • [1] D. Yin, K. Zhang, G. Wang, W. Han, Mater. Sci. Eng. A 392, 320 (2005)
  • [2] A. El-Morsy, A. Ismail, M. Waly, Mater. Sci. Eng. A 486, 528 (2008)
  • [3] M. Shahzad, L. Wagner, Fatig. Eng. Mater. Struct. 33, 221 (2010)
  • [4] J. Müller, M. Janeček, L. Wagner, Mater. Sci. Forum 584-586, 858 (2008)
  • [5] H. Takamura, T. Miyashita, A. Kamegawa, M. Okada, J. Alloys Comp. 356-357, 804 (2003)
  • [6] D. Arpacy, S. Yi, M. Janecek, A. Bakkaloglu, L. Wagner, Mater. Sci. Forum 584-586, 300 (2008)
  • [7] M.Z. Oo, J. Mueller, M. Janecek, L. Wagner, Int. J. Mater. Res. 100, 374 (2009)
  • [8] Z. Horita, K. Ohashi, T. Fujita, K. Kaneko, T.G. Langdon, Adv. Mater. 17, 1599 (2005)
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv122z3p44kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.