2012 | 122 | 3 | 581-587
Article title

FEA of Plastic Flow in AZ63 Alloy during ECAP Process

Content
Title variants
Languages of publication
EN
Abstracts
EN
Magnesium alloys based on Mg-Al-Zn system are very attractive materials in many industries due to their specific properties. One of common forming manners suitable for this kind of material is the application of severe plastic deformation method. This paper is focused on the deformation behavior of AZ63 alloy at equal channel angular pressing process in the temperature range of 250-320°C. For this purpose finite element analysis was used. Main attention was devoted to the influence of processing parameters on the material flow. Among other, changes of the flow during equal channel angular pressing in chosen regions of the pressed samples were monitored. As variables, temperature, friction coefficient, strain rate, φ-angle or back pressure application were chosen. The comparison of the material flow lines at different conditions shows the affecting of material flow. There are obvious considerable differences between regions adjacent to the inner radius and those adjacent to the outer radius. For example in the case μ = 0 the dead zone is delimited by the angle Ψp = 36°, while in the case of friction given by the coefficient μ = 0.04, the value of the angle was Ψp = 26.5°.
Keywords
Contributors
author
  • Department of Materials Forming, Faculty of Metallurgy and Materials Engineering, VŠB TU Ostrava, 17. listopadu 15, CZ 70833 Ostrava-Poruba, Czech Republic
author
  • Department of Non Ferrous Metals Refining and Recycling, Faculty of Metallurgy and Materials Engineering, VŠB TU Ostrava, 17. listopadu 15, CZ 70833 Ostrava-Poruba, Czech Republic
  • Department of Thermal Engineering, Faculty of Metallurgy and Materials Engineering, VŠB TU Ostrava, 17. listopadu 15, CZ 70833 Ostrava-Poruba, Czech Republic
References
  • [1] M. Furukawa, Z. Horita, M. Nemoto, R.Z. Valiev, T.G. Langdon, Philos. Mag. A 78, 203 (1998)
  • [2] M.V. Markushev, C.C. Bampton, M.Y. Murashkin, D.A. Hardwick, Mater. Sci. Eng. A 234-235, 927 (1997)
  • [3] R. Kocich, M. Kursa, I. Szurman, A. Dlouhý, J. Alloys Comp. 509, 2716 (2011)
  • [4] R. Kocich, J. Fiala, I. Szurman, A. Macháčková, M. Mihola, J. Mater. Sci. 46, 7865 (2011)
  • [5] E. Hosseini, M. Kazeminezhad, Comput. Mater. Sci. 44, 962 (2009)
  • [6] N. Mahallawy, F.A. Shehata, M. Hameed, M.I. Aal, H.S. Kim, Mater. Sci. Eng. A 527, 1404 (2010)
  • [7] W.J. Kim, S.I. Hong, Y.S. Kim, S.H. Min, H.T. Jeong, J.D. Lee, Acta Mater. 51, 3293 (2003)
  • [8] M. Mabuchi, H. Iwasaki, K. Yanase, K. Higashi, Scr. Mater. 36, 681 (1997)
  • [9] A. Ma, J. Jiang, N. Saito, I. Shigematsu, Y. Juan, D. Yang, Y. Nishida, Mater. Sci. Eng. A 513-514, 122 (2009)
  • [10] J.C. Tan, M.J. Tan, Mater. Sci. Eng. A 339, 124 (2003)
  • [11] S.L. Semiatin, V.M. Segal, R.E. Goforth, N.D. Frey, D.P. DeLo, Metall. Mater. Trans. 30A, 1425 (1999)
  • [12] M. Furui, H. Kitamura, H. Anada, T.G. Langdon, Acta Mater. 55, 1083 (2007)
  • [13] R.B. Figueiredo, P.R. Cetlin, T.G. Langdon, Acta Mater. 55, 4769 (2007)
  • [14] V.V. Stolyarov, R. Lapovok, I.G. Brodova, P.F. Thomson, Mater. Sci. Eng. A 357, 159 (2003)
  • [15] R.B. Figueiredo, P.R. Cetlin, T.G. Langdon, Metall. Mater. Trans. 41A, 778 (2010)
  • [16] Z. Horita, K. Matsubara, K. Makii, T.G. Langdon, Scr. Mater. 47, 255 (2002)
  • [17] Y. Miyahara, Z. Horita, T.G. Langdon, Mater. Sci. Eng. A 420, 240 (2006)
  • [18] V.M. Segal, Mater. Sci. Eng. A 345, 36 (2003)
  • [19] G.M. Stoica, D.E. Fielden, R. McDaniels, Y. Liu, B. Huang, P.K. Liaw, C. Xu, T.G. Langdon, Mater. Sci. Eng. A 410-411, 239 (2005)
  • [20] R.B. Figuiredo, P.R. Cetlin, T.G. Langdon, Mater. Sci. Eng. A 518, 124 (2009)
  • [21] H.S. Kim, Mater. Sci. Eng. A 328, 317 (2002)
  • [22] R. Kocich, M. Greger, A. Macháčková, in: Proc. Conf. Metal, TANGER, Ostrava 2010, p. 166
  • [23] S.E. Ion, F.J. Humpreys, S.H. White, Acta Metall. 30, 1909 (1982)
  • [24] A.V. Nagasekhar, T.H. Yip, S. Li, H.P. Seow, Mater. Sci. Eng. A 410-411, 269 (2005)
  • [25] H.S. Kim, S.I. Hong, M.H. Seo, J. Mater. Res. 16, 856 (2001)
  • [26] J.W. Park, J.Y. Suh, Metall. Mater. Trans. 32A, 3007 (2001)
  • [27] J.C. Werenskiold, H.J. Roven, in: Proc. Conf. 'Nanomaterials by Severe Plastic Deformation - NANOSPD2', Vienna (Austria), 2002, p. 591
  • [28] M.G. Cockroft, D.J. Latham, J. Inst. Metals 96, 33 (1968)
  • [29] R.K. Oruganti, P.R. Subramanian, J.S. Marte, M.F. Gigliotti, S. Amancherla, Mater. Sci. Eng. A 406, 102 (2005)
  • [30] F. Djavanroodi, M. Ebrahimi, Mater. Sci. Eng. A 527, 1230 (2010)
  • [31] P.W.J. Mckenzie, R. Lapovok, Y. Estrin, Acta Mater. 55, 2985 (2007)
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv122z3p39kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.