Anelastic Phenomena in Mg-Al Alloys

Content
Title variants
Languages of publication
EN
Abstracts
EN
Cyclic loading-unloading in tension and compression has been used to quantify the anelastic behaviour, in the form of hysteresis loops, of pure Mg and three Mg-Al alloys (0.5, 2, and 9 at.% Al). The effect reached a maximum at a plastic strain of ≈ 0.02 for all of the materials, and decreased at higher strains. The amount of anelasticity at any given strain was smaller for the dilute alloys in comparison with the pure Mg whereas it increased above that of pure Mg for the most concentrated alloy. Possible reasons for this behaviour are discussed in terms of reversible twinning, solid solution softening, and hardening and short range order.
Keywords
Contributors
author
  • ARC-Centre of Excellence for Design in Light Metals, Materials Engineering, School of Engineering, The University of Queensland, Brisbane, QLD 4072, Australia
author
  • ARC-Centre of Excellence for Design in Light Metals, Materials Engineering, School of Engineering, The University of Queensland, Brisbane, QLD 4072, Australia
author
  • CSIRO Process Science & Engineering, P.O. Box 883, Kenmore, QLD 4069, Australia
References
  • [1] C.H. Cáceres, T. Sumitomo, M. Veidt, Acta Mater. 51, 6211 (2003)
  • [2] G.E. Mann, T. Sumitomo, C.H. Cáceres, J.R. Griffiths, Mater. Sci. Eng. 456A, 138 (2007)
  • [3] R.E. Reed-Hill, E.P. Dahlberg, W.A. Slippy, Jr., Trans. Metall. Soc. AIME 233, 1766 (1965)
  • [4] T.W. Duerig, R. Zadno, An engineer's perspective of pseudoelasticity, in: Engineering Aspects of Shape Memory Alloys, Ed. T.W. Duerig, Butterworth-Heineman, 1990, p. 369
  • [5] M.A. Gharghouri, G.C. Weatherly, J.D. Embury, J. Root, Philos. Mag. 79, 1671 (1999)
  • [6] M.A. Gharghouri, Ph.D. Thesis, McMaster University, Hamilton, Ontario 1996
  • [7] R.L. Woolley, J. Inst. Met. 83, 57 (1954)
  • [8] Z. Keshavarz, M.R. Barnett, in: Magnesium Technology 2005, Eds. N.R. Neelameggham, H.I. Kaplan, B.R. Powell, TMS (The Minerals, Metals and Materials Society), San Francisco, CA, 2005, p. 171
  • [9] S.R. Agnew, M.H. Yoo, C.N. Tomé, Acta Mater. 49, 4277 (2001)
  • [10] A. Akhtar, E. Teghtsoonian, Acta Metall. 17, 1351 (1969)
  • [11] C.H. Cáceres, A. Blake, Phys. Status Solidi A 194, 147 (2002)
  • [12] C.H. Cáceres, D.M. Rovera, J. Light Met. 1/3, 151 (2001)
  • [13] G.W. Groves, A. Kelly, P. Kidd, Crystallography and Crystal Defects, Wiley, West Sussex 2000, Ch. 10
  • [14] J.W. Cahn, Acta Metall. 25, 1021 (1977)
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv122z3p19kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.