2012 | 121 | 1 | 89-93
Article title

Magnetic Properties of Nd_{12}Fe_{82}B_6 and Nd_{14}Fe_{80}B_6 Powders Obtained by High Temperature Milling

Content
Title variants
Languages of publication
EN
Abstracts
EN
The present paper describes a comparison of magnetic properties of Nd_{12}Fe_{82}B_6 and Nd_{14}Fe_{80}B_6 powders obtained by a new method of processing of Nd-Fe-B powders - high temperature milling. In this method the milling operation is carried out, entirely or only in the final stage, at high temperatures, so that the destruction of the Nd_2Fe_{14}B phase and its recombination occur simultaneously. In this way a powder with good magnetic properties immediately after milling was obtained. In the present experiments, the powder was subjected to high-energy milling for 17 h (until the material becomes amorphous) and then, the milling was continued for 0.5 h with the powder container being heated to an appropriate temperature or milled at high temperature during whole time of the process. Diffraction examinations have shown that the powder processed in this way contains the Nd_2Fe_{14}B phase. Its magnetic properties appear to depend on the applied temperature or milling time (at optimum temperature). The used method of processing leads to obtaining high-coercivity Nd-Fe-B powders. The magnetic properties of the material thus produced, in particular its coercivity, strongly depend on the milling temperature and milling time.
Keywords
EN
Contributors
author
  • Faculty of Materials Science and Engineering, Warsaw University of Technology, Wołoska 141, 02-507 Warsaw, Poland
author
  • Faculty of Materials Science and Engineering, Warsaw University of Technology, Wołoska 141, 02-507 Warsaw, Poland
References
  • 1. A. Calka, D. Wexler, Nature 419, 147 (2002)
  • 2. A. Calka, Rev. Adv. Mater. Sci. 18, 398 (2008)
  • 3. S. Zghal, R. Twesten, Fang Wu, P. Bellon, Acta Mater. 50, 4711 (2002)
  • 4. W. Kaszuwara, B. Michalski, to be published in Lat. Am. Phys. Educ
  • 5. W. Kaszuwara, B. Michalski, Inżynieria Materiałowa 179, 9 (2011) (in Polish)
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv121n126kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.