Different Wavelength Laser Irradiation of Amorphous Carbon

Content
Title variants
Languages of publication
EN
Abstracts
EN
Coherent laser irradiation of amorphous carbon films formed on Si substrates by ion beam deposition from pure acetylene and acetylene/hydrogen gas mixture is analyzed in this work. The films were irradiated with nanosecond YAG:Nd laser (Ekspla NL301G) at the first (1064 nm, 6 ns), the second (532 nm, 4.2 ns) and the third (355 nm, 28 ns) harmonic by scanning or repeating (10 pulses to one point) regime. Irradiation by the first laser harmonic leads to a minor increase of graphite phase content and shows SiC formation. Formation of carbides was observed at the second harmonic irradiation when irradiation intensity is low (< 10 MW/cm^2). Graphitization became more intensive when power density of irradiation increased and the films transformed to the glass carbon and nano/micro crystallite compound at intensive ablation regime ( ≈ 24 MW/cm^2). Early ablation starts at irradiation by the third laser harmonic with the intensity of ≈ 8 MW/cm^2 with an increase of Si substrate roughness. Swelling of films was obtained when the sample was irradiated at the third harmonic with 1 MW/cm^2.
Keywords
Year
Volume
120
Issue
1
Pages
26-29
Physical description
Dates
published
2011-07
References
  • 1. K.P. Chu, L. Li, Mater. Chem. Phys. 96, 253 (2006)
  • 2. J. Robertson, J. Mater. Sci. Eng. R 37, 129 (2002)
  • 3. M.G. Beghi, A.C. Ferrari, K.B.K. Teo, J. Robertson, C.E. Bottani, A. Libassi, B.K. Tanner, Appl. Phys. Lett. 81, 3804 (2002)
  • 4. T.V. Kononenko, V.G Ralchenko, E.D Obraztsova, V.I. Konov, J. Seth, S.V Babu, Appl. Surf. Sci. 86, 234 (1995)
  • 5. T.V. Kononenko, V.V. Kononenko, S.M. Pimenov, E.V. Zavedeev, V.I. Konov, V. Romano, G. Dumitru, Diamond Relat. Mater. 14, 1368 (2005)
  • 6. S.K. Sundaram, E. Mazur, Nat. Mater. 1, 217 (2002)
  • 7. R. Le Harzic, N. Huot, E. Audouard, C. Jonin, P. Laporte, S. Valette, A. Franczkiewicz, R. Forturier, Appl. Phys. Lett. 80, 3886 (2002)
  • 8. G. Daminelli, S. Pentzien, A. Hertwig, J. Kruger, Appl. Phys. A 83, 89 (2006)
  • 9. E. Cappelli, C. Scilletta, S. Orlando, V. Valentini, M. Servidori, Appl. Surf. Sci. 255, 5620 (2009)
  • 10. L.H. Zang, J.P Wang, H. Gong, J. Phys., Condens. Matter 13, 2989 (2001)
  • 11. A. Grigonis, Ž. Rutkunienė, A. Medvids, Vacuum 82, 1212 (2008)
  • 12. D. Vouagner, Cs. Beleznai, J.P. Girardeau-Montaut, C. Templier, H. Gonnord, Appl. Surf. Sci. 201, 154 (2000)
  • 13. A. Grigonis, A. Medvid, P. Onufrijevs, J. Babonas, A. Rėza, Opt. Mater. 30, 749 (2008)
  • 14. A. Grigonis, Ž. Rutkūniene, V. Kaminskas, in: Conf. Proc. Radiation Interaction with Material and Its Use in Technologies, Technologija, Kaunas 2008, p. 123
  • 15. J. Ristein, R.T. Stief, L. Ley, W. Beyer, J. Appl. Phys. 84, 3836 (1998)
  • 16. W. Wei, Vacuum 81, 857 (2007)
Document Type
Publication order reference
YADDA identifier
bwmeta1.element.bwnjournal-article-appv120n106kz
Identifiers
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.