Content
Title variants
Languages of publication
EN
Abstracts
EN
The aim of this work was to investigate the influence of resin content on AC magnetic properties of Vitroperm 800-based composite material to extend possibilities for application of this kind of material at higher frequency (up to 100 kHz). The samples of composite material were prepared in the form of the ring with outer diameter of 25 mm, inner diameter of 18 mm and height approximately 3 mm. Powder mixtures were prepared from Vitroperm 800 in partial nanocrystalline state and commercial termoset resins by mechanical mixing. The AC magnetic properties (losses) at maximum induction up to 0.5 T were measured by MATS-2010SA loop tracer in frequency range 1-100 kHz. The specific resistivity of the material was measured by the van der Pauw method. The magnetic properties of the composite rings were compared with the properties of the material prepared from Fe based powder supported by Höganäs. It was found out that the total losses of the Vitroperm-based soft magnetic composite are more than 10 times lower (at 10 kHz) than that for Fe-based one.
Keywords
Year
Volume
118
Issue
5
Pages
787-789
Physical description
Dates
published
2010-11
References
  • 1. T. Maeda, H. Tyoda, N. Igarashi, K. Hirose, K. Mimura, T. Nishioka, A. Ikegaya, SEI Tech. Rev. 60, 3 (2005)
  • 2. H. Shokrollahi, K. Janghorban, J Mater. Proc. Technol. 189, 1 (2007)
  • 3. B. Weidenfeller, M. Anhalt, W. Riehemann, J. Magn. Magn. Mater. 320, e382 (2008)
  • 4. D. Nuetzel, G. Rieger, J. Wecker, J. Petzold, M. Mueller, J. Magn. Magn. Mater. 196-197, 327 (1999)
  • 5. http://www.vacuumschmelze.de
  • 6. Product catalog: Somaloy® Metal Powders for SMC Components, Höganäs AB, Sweden
  • 7. P. Kollár, J. Füzer, R. Bureš, M. Fáberová, IEEE Trans. Magn. 46, 467 (2010)
  • 8. L.J. van der Pauw, Philips Techn. Rev. 20, 220 (1958)
  • 9. R.M. Bozorth, Ferromagnetism, 3rd ed, IEEE Press, Piscataway (NJ) 1993
  • 10. T.D. Shen, U. Harms, R.B. Schwarz, Mater. Sci. Forum 386-388, 441 (2002)
Document Type
Publication order reference
YADDA identifier
bwmeta1.element.bwnjournal-article-appv118n5030kz
Identifiers
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.