XPS Investigation of Y_{1-x}Dy_xNi_2B_2C Superconductors

• Authors: A. Winiarski , A. Winiarska , Z. Drzazga
• Languages of publication: EN

Abstracts

EN

The analysis of the valence band photoemission spectra of Y_{1-x}Dy_xNi_2B_2C (0≤x≤1) is presented. The valence bands are mainly plotted for Ni 3d, Y 4d and Dy 4f contributions, according to theoretical predictions. The valence bands of Y_{1-x}Dy_xNi_2B_2C compounds markedly change shape with the x parameter, especially in the binding energy region from 3 eV to 14 eV. For large content of Dy (above 55%) the valence band is predominant by Dy 4f states whereas Ni 3d states govern the valence band of yttrium rich compounds. Changing in domination of valence sub-band correlates with plot of superconducting transition temperature T_c with Dy concentration.

Keywords

EN

71.20.-b; 74.25.Jb; 74.70.-b; 82.80.Pv

Discipline

• 71.20.-b: Electron density of states and band structure of crystalline solids
• 74.25.Jb: Electronic structure (photoemission, etc.)
• 74.70.-b: Superconducting materials other than cuprates(for cuprates, see 74.72.-h; for superconducting films, see 74.78.-w)
• 82.80.Pv: Electron spectroscopy (X-ray photoelectron (XPS), Auger electron spectroscopy (AES), etc.)

• Journal: Acta Physica Polonica A
• Year: 2008
• Volume: 114
• Issue: 1
• Pages: 243-246

Dates

published

2008-07

received

2007-11-06

Contributors

author

A. Winiarski

• August Chełkowski Institute of Physics, Uniwersytecka 4, 40-007 Katowice, Poland

author

A. Winiarska

• August Chełkowski Institute of Physics, Uniwersytecka 4, 40-007 Katowice, Poland

author

Z. Drzazga

• August Chełkowski Institute of Physics, Uniwersytecka 4, 40-007 Katowice, Poland

References

• 1. M.D. Lan, T.J. Chang, C.S. Liaw, J. Phys. Chem. Solids 59, 1285 (1998)
• 2. P. Allenspach, U. Gasser, J. Alloys Comp. 311, 1 (2000)
• 3. J. Freudenberger, G. Fuchs, K. Nenkov, S.-L. Drechsler, K.-H. Műhler, L. Schultz, Physica C, Superconductivity 339, 195 (2000)
• 4. S.M. Loureiro, C. Kealhofer, C. Felser, R.J. Cava, Solid State Commun. 119, 675 (2001)
• 5. K.-H. Műller, V.N. Narozhnyi, Rep. Prog. Phys. 64, 943 (2001)
• 6. A.O. Shorikov, V.I. Anisimov, M. Sigrist, J. Phys., Condens. Matter 18, 5973 (2006)
• 7. J.I. Lee, T.S. Zhao, I.G. Kim, B.I. Min, S.J. Youn, Phys. Rev. B 50, 4030 (1994)
• 8. Z. Drzazga, A. Winiarska, A. Winiarski, D. Kaczorowski, Acta Phys. Pol. A 97, 221 (2000)
• 9. Z. Drzazga, D. Kaczorowski, A. Winiarska, A. Winiarski, J. Alloys Comp. 323-324, 562 (2001)
• 10. Z. Drzazga, A. Winiarska, D. Kaczorowski, J. Magn. Magn. Mater. 242-245, 829 (2002)
• 11. L.F. Mattheiss, High-T_c Update 8, 2 (1994)
• 12. K. Yamauchi, H. Katayama-Yoshida, A. Yanase, H. Harima, Physica C 412-414, 225 (2004)
• 13. J. Wang, X. Zhang, Y. Ruan, Z. Jiao, Q. Zhang, Ch. Fan, X. Zhang, Y. Su, G. Cao, Physica C 282-287, 1935 (1997)
• 14. L.-S. Hsu, C.-J. Chen, M.-D. Lan, J. Alloys Comp. 397, 23 (2005)

Identifiers

DOI

10.12693/APhysPolA.114.243