2008 | 113 | 1 | 119-122
Article title

Perminvar Effect in Amorphous Hitperm Alloy

Content
Title variants
Languages of publication
EN
Abstracts
EN
Influence of the directional ordering on magnetization processes in the amorphous Fe_{44.5}Co_{44.5}Zr_7B_4 alloy was investigated in the temperature region of 27 to 300°C for stabilization times of up to 1000 min by means of the Perminvar effect. The time-temperature dependent Perminvar effect was found to be very sensitive on the stage of the domain structure stabilization. The Perminvar critical fields H_{CR} were shifted to higher values with increasing stabilization temperatures and times. At lower temperatures, the susceptibility increases over wide range of the measuring fields. Stabilization at higher temperatures causes that the susceptibility abruptly increases in the narrow field range. The record critical field H_{CR} =246 Am^{-1} was obtained.
Keywords
EN
Publisher

Year
Volume
113
Issue
1
Pages
119-122
Physical description
Dates
published
2008-01
received
2007-07-09
Contributors
author
  • Institute of Physics, Fac. Sci., P.J. Šafárik University, Park Angelinum 9, 041 54 Košice, Slovakia
author
  • Institute of Physics, Fac. Sci., P.J. Šafárik University, Park Angelinum 9, 041 54 Košice, Slovakia
author
  • Institute of Physics, Fac. Sci., P.J. Šafárik University, Park Angelinum 9, 041 54 Košice, Slovakia
author
  • Faculty of Aeronautics, Technical University, Rampová7, 041 21 Košice, Slovakia
References
  • 1. M.E. McHenry, M.A. Willard, D.E. Laughlin, Prog. Mater. Sci. 44, 291 (1999)
  • 2. R. Andrejco, P. Vojtanik, J. Phys., Condens. Matter 16, 3745 (2004)
  • 3. P. Vojtanik, J. Magn. Magn. Mater. 304, 159 (2006)
  • 4. G.W. Elmen, J. Franklin Inst. 207, 583 (1929)
  • 5. L. Néel, J. Phys. Radium 13, 249 (1952)
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv113n1029kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.