2008 | 113 | 1 | 103-106
Article title

Study of Stress-Annealing Enhancement of Magnetoimpedance Effect in Fe_{89.8}Ni_{1.5}Si_{5.2}B_{3}C_{0.5} Metallic Glass Ribbons

Content
Title variants
Languages of publication
EN
Abstracts
EN
In this study, the magnetoimpedance effect in magnetically soft Fe_{89.8}Ni_{1.5}Si_{5.2}B_{3}C_{0.5} metallic glass ribbon samples with significant decrease in atomic percentage of metalloids content (less than 10 at.%) was investigated. Thermal treatments were performed by stress-annealing technique of up to 693 K/475 MPa/30 min. The critical frequency of about 600 kHz was observed as the point with the initial increase in magnetoimpedance ratio. Significant improvement of magnetoimpedance-response reaching the value ΔZ/Z=25% after stress-annealing at 693 K/130 MPa/30 min was recorded in samples with still amorphous structure at driving frequency of 4 MHz. The highest magnetoimpedance-element sensitivity was found for low magnetic field intensity (H ≤ 1 kA/m), where values of about 12%/kA/m were attained.
Keywords
EN
Publisher

Year
Volume
113
Issue
1
Pages
103-106
Physical description
Dates
published
2008-01
received
2007-07-09
Contributors
  • Joint Laboratory for Advanced Materials of SASA, Section for Amorphous Materials, Technical Faculty Čačak, Svetog Save 65, 32 000 Čačak, Serbia
author
  • Joint Laboratory for Advanced Materials of SASA, Section for Amorphous Materials, Technical Faculty Čačak, Svetog Save 65, 32 000 Čačak, Serbia
author
  • Joint Laboratory for Advanced Materials of SASA, Section for Amorphous Materials, Technical Faculty Čačak, Svetog Save 65, 32 000 Čačak, Serbia
author
  • Joint Laboratory for Advanced Materials of SASA, Section for Amorphous Materials, Technical Faculty Čačak, Svetog Save 65, 32 000 Čačak, Serbia
  • Joint Laboratory for Advanced Materials of SASA, Section for Amorphous Materials, Technical Faculty Čačak, Svetog Save 65, 32 000 Čačak, Serbia
References
  • 1. R.L. Sommer, C.L. Chien, Appl. Phys. Lett. 67, 857 (1995)
  • 2. K. Mohri, K. Bushida, M. Noda, L.V. Panina, T. Uchiyama, IEEE Trans. Magn. MAG-31, 2455 (1995)
  • 3. N. Mitrović, S. Roth, S. Kane, Mater. Sci. Forum 518, 313 (2006)
  • 4. N. Mitrović, Sci. Sintering Spec. Issue 30, 85 (1998)
  • 5. A. Kalezić-Glišović, L. Novaković, A. Maričić, D. Minić, N. Mitrović, Mater. Sci. Eng. B 131, 45 (2006)
  • 6. J.M. Barandiaran, A. Garcia-Aribes, J.L. Muza, G.V. Kurlyandskaya, IEEE Trans. Magn. MAG-38, 3051 (2002)
  • 7. M. Vàzquez, G.V. Kurlyandskaya, J.M. Garcia-Beneytez, J.P. Sinnecker, J.M. Barandiaran, V.A. Lukshina, A.P. Potatova, IEEE Trans. Magn. MAG-35, 3358 (1999)
  • 8. M.N. Gona, S. Yanase, S. Hashi, Y. Okozaki, J. Magn. Magn. Mater. 254-255, 466 (2003)
  • 9. L. Kraus, Sensors Actuators A 106 , 187 (2003)
Document Type
Publication order reference
Identifiers
YADDA identifier
bwmeta1.element.bwnjournal-article-appv113n1025kz
JavaScript is turned off in your web browser. Turn it on to take full advantage of this site, then refresh the page.