In Situ Energy Dispersive X-Ray Diffraction Analysis of the Temperature-Pressure Stability of Co-Fe-(Ta,W)-B Alloys

• Authors: R. Kanász , J. Bednarčík , K. Saksl , R. Nicula , M. Stir , C. Lathe
• Languages of publication: EN

Abstracts

EN

In this work two Co_{53.5}Fe_{10}X_{5.5}B_{31} (X = Ta, W) alloys were synthesized from high purity (≥99.9%) powder elements by means of mechanical alloying. In case of Ta-addition, mechanical alloying resulted in formation of two component material with nanocrystalline phase embedded in amorphous matrix. On the other hand, substitution of Ta by W retards partial amorphization induced by mechanical alloying. High pressure-temperature stability of both alloys was monitored using in situ energy dispersive X-rays.

Keywords

EN

75.50.Kj

Discipline

• 75.50.Kj: Amorphous and quasicrystalline magnetic materials

• Publisher: Institute of Physics, Polish Academy of Sciences
• Journal: Acta Physica Polonica A
• Year: 2008
• Volume: 113
• Issue: 1
• Pages: 79-82

Dates

published

2008-01

received

2007-07-09

Contributors

author

R. Kanász

• Institute of Physics, Faculty of Science, P. J. Šafárik University, Park Angelinum 9, 041 54 Košice, Slovak Republic

author

J. Bednarčík

• Deutsches Elektronen Synchrotron (HASYLAB), Notkestraße 85, 22607 Hamburg, Germany

author

K. Saksl

• Deutsches Elektronen Synchrotron (HASYLAB), Notkestraße 85, 22607 Hamburg, Germany
• Institute of Materials Research, Slovak Academy of Sciences, Watsonova 47, 043 53 Košice, Slovak Republic

author

R. Nicula

• University of Rostock, Institute of Physics, August-Bebel-Str. 55, 18055 Rostock, Germany

author

M. Stir

• University of Rostock, Institute of Physics, August-Bebel-Str. 55, 18055 Rostock, Germany

author

C. Lathe

• GeoForschungsZentrum Potsdam at DESY/HASYLAB

References

• 1. A. Inoue, B. Shen, H. Koshiba, H. Kato, A.R. Yavari, Nature Mater. 2, 661 (2003)
• 2. A. Inoue, B.L. Shen, H. Koshiba, H. Kato, A.R. Yavari, Acta Mater. 52, 1631 (2004)
• 3. J. Bednarčík, P. Kollár, S. Roth, J. Eckert, Phys. Status Solidi A 199, 299 (2003)
• 4. M. Stir, R. Nicula, E. Burkel, J. Eur. Ceram. Soc. 26, 1547 (2006)
• 5. D. L. Decker, J. Appl. Phys. 42, 3239 (1971)

Identifiers

DOI

10.12693/APhysPolA.113.79